Publication detail
Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region
LUKÁŠ, P. KUNZ, L. NAVRÁTILOVÁ, L. BOKŮVKA, O.
Czech title
Únavové poškození ultrajemnozrnné mědi při gigacyklovém zatěžování
English title
Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region
Type
journal article - other
Language
en
Original abstract
Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.
Czech abstract
Ultrajemnozrnná měď připravená metodou ECAP byla testována v gigacyklovém zatěžovácím režimu v rozmezí počtu cyklů 10^8 až 2x10^10. Únavová pevnost ultrajemnozrnné mědi je dvakrát vyšší než v případě mědi s konvenční velikostí zrna. Výskyt skluzových pásů na povrchu vzorků je velice řídký. Nebylo pozorováno žádné hrubnutí zrna ani na "bulkovém" materiálu, ani v oblastech pod skluzovými pásy. Jako hlavní mechanismus vedoucí k iniciaci únavových trhlin je považován skluz po hranicích zrn s přibližně stejnou orientací v oblasti pod skluzovými pásy.
English abstract
Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.
Keywords in Czech
gigacyklová únava, UFG měď, skluzové pásy, iniciace únavových trhlin
Keywords in English
very-high cycle region, fatigue, UFG copper, slip markings, crack initiation
RIV year
2011
Released
25.04.2011
ISSN
0921-5093
Volume
528
Number
22-23
Pages from–to
7036–7040
Pages count
5
BIBTEX
@article{BUT88368,
author="Petr {Lukáš} and Ludvík {Kunz} and Lucie {Navrátilová} and Otakar {Bokůvka},
title="Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region",
year="2011",
volume="528",
number="22-23",
month="April",
pages="7036--7040",
issn="0921-5093"
}