Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.

Český abstrakt

Ultrajemnozrnná měď připravená metodou ECAP byla testována v gigacyklovém zatěžovácím režimu v rozmezí počtu cyklů 10^8 až 2x10^10. Únavová pevnost ultrajemnozrnné mědi je dvakrát vyšší než v případě mědi s konvenční velikostí zrna. Výskyt skluzových pásů na povrchu vzorků je velice řídký. Nebylo pozorováno žádné hrubnutí zrna ani na "bulkovém" materiálu, ani v oblastech pod skluzovými pásy. Jako hlavní mechanismus vedoucí k iniciaci únavových trhlin je považován skluz po hranicích zrn s přibližně stejnou orientací v oblasti pod skluzovými pásy.

Anglický abstrakt

Ultrafine-grained copper produced by ECAP technique was tested in ultrasonic fatigue in the region of lives from 10^8 to 2x10^10 cycles. The fatigue strength of ultrafine-grained copper is by a factor of 2 higher than that of conventional-grain copper. The occurrence of surface fatigue slip markings is rare. No grain coarsening was observed either in bulk or in areas underneath the surface slip markings. Localized collective grain-boundary slip of near-by oriented grains is considered to be the main damage mechanism leading to fatigue microcrack initiation either directly in the roots of surface intrusions or underneath the surface slip markings.

Klíčová slova česky

gigacyklová únava, UFG měď, skluzové pásy, iniciace únavových trhlin

Klíčová slova anglicky

very-high cycle region, fatigue, UFG copper, slip markings, crack initiation

Rok RIV

2011

Vydáno

25.04.2011

ISSN

0921-5093

Ročník

528

Číslo

22-23

Strany od–do

7036–7040

Počet stran

5

BIBTEX


@article{BUT88368,
  author="Petr {Lukáš} and Ludvík {Kunz} and Lucie {Navrátilová} and Otakar {Bokůvka},
  title="Fatigue damage of ultrafine-grain copper in very-high cycle fatigue region",
  year="2011",
  volume="528",
  number="22-23",
  month="April",
  pages="7036--7040",
  issn="0921-5093"
}