Publication detail
Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life
SLÁMEČKA, K. KIANICOVÁ, M. POKLUDA, J.
Czech title
Fraktografie trhlin typu "rybí oko" v nitridované oceli: posouzení reziduální únavové životnosti
English title
Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life
Type
journal article - other
Language
en
Original abstract
An assessment of the residual fatigue life of plasma-nitrided high-strength low-alloy steel specimens has been performed. The study combines fractographical observation of the local striations field found in the centre of the fish-eye crack of the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack growth. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the crack initiation. This conclusion is consistent with the high- and ultra-high-cycle behaviour of specimens without any surface hardening layer.
Czech abstract
Článek se zabývá posouzením reziduální únavové životnosti plasmově nitridovaných zkušebních těles vyrobených z vysocepevné nízkolegované oceli. Informace zjištěné mikrofraktografickým rozborem lokálního pole únavových striací situovaného v těsné blízkosti inkluze ve středu trhliny typu "rybí oko" jsou využity v modelu růstu únavové trhliny, který je založen na lineární elastické lomové mechanice. Z výsledků je zřejmé, že etapa šíření představuje pouze minoritní část celkové únavové životnosti, jejíž dominantní sloužkou je tudíž etapa iniciace únavové trhliny. Tento závěr je konzistentní s únavovým chováním hladkých zkušebních těles bez jakékoliv zpevňující vrstvy v obou vysokocyklové a gigacyklové oblasti.
English abstract
An assessment of the residual fatigue life of plasma-nitrided high-strength low-alloy steel specimens has been performed. The study combines fractographical observation of the local striations field found in the centre of the fish-eye crack of the specimen subjected to combined bending-torsion loading with the linear elastic fracture mechanics modelling of the fatigue crack growth. The results suggest that the propagation stage constitutes only a minor part of the total fatigue life, the major part of which is spent on the crack initiation. This conclusion is consistent with the high- and ultra-high-cycle behaviour of specimens without any surface hardening layer.
Keywords in Czech
kvantitativní fraktografie, rybí oka, striace, lineární elastická lomová mechanika, nitridovaná ocel
Keywords in English
Fractography, fish-eye cracks, striations, linear elastic fracture mechanics, nitrided steel
RIV year
2011
Released
01.08.2011
Location
Opole
ISSN
1429-6055
Volume
z98
Number
1
Pages from–to
1–10
Pages count
10
BIBTEX
@article{BUT76083,
author="Karel {Slámečka} and Marta {Kianicová} and Jaroslav {Pokluda},
title="Fractography of Fish-eye Cracks in Nitride Steel Specimens: Assessment of Residual Fatigue Life",
year="2011",
volume="z98",
number="1",
month="August",
pages="1--10",
address="Opole",
issn="1429-6055"
}