CYCLIC DEFORMATION RESPONSE OF AZ31 MAGNESIUM ALLOY AFTER CORROSION DEGRADATION
DOLEŽAL, P. ZAPLETAL, J. HORYNOVÁ, M. GEJDOŠ, P. ČELKO, L.
Czech title
CYKLICKÁ DEFORMAČNÍ ODEZVA HOŘČÍKOVÉ SLITINY AZ31 PO KOROZNÍ DEGRADACI
English title
CYCLIC DEFORMATION RESPONSE OF AZ31 MAGNESIUM ALLOY AFTER CORROSION DEGRADATION
Type
journal article - other
Language
en
Original abstract
Cyclic deformation response and low cycle fatigue behaviour of bare and pre-corroded magnesium alloy AZ31 was studied under stress amplitude control. Pre-corroded specimens had been exposed to spray of 5 % solution of sodium chloride for 480 and 1000 hours. Fatigue limit drops from 52.1 Mpa to 47.5 MPa (480 hrs) and 38.4 (1000 hrs). Fatigue life decrease due to corrosion damage is pronounced at loww stress amplitudes, whereas the durability attained at higher amplitudes is practically the same.
Czech abstract
Cyklická deformační odezva a únavové chování v nízkocyklové oblasti bylo studováno u slitiny AZ31 v základním stavu a po korozní degradaci. Únavové zkoušky probíhaly v módu řízené amplitudy napětí. Únavová zkušební tělesa byla podrobena korozní degradaci v korozní komoře s mlhou 5% roztoku chloridu sodného a dobou expozice 480 a 1000 hodin. Mez únavy poklesla z 52,1 MPa na 47,5 MPa (480 hod) a 38,4 MPa (1000 hod). Pokles únavové životnosti v důsledku korozního napadení je výraznější na nižších amplitudách napětí, na vyšších hladinách je životnost prakticky stejná.
English abstract
Cyclic deformation response and low cycle fatigue behaviour of bare and pre-corroded magnesium alloy AZ31 was studied under stress amplitude control. Pre-corroded specimens had been exposed to spray of 5 % solution of sodium chloride for 480 and 1000 hours. Fatigue limit drops from 52.1 Mpa to 47.5 MPa (480 hrs) and 38.4 (1000 hrs). Fatigue life decrease due to corrosion damage is pronounced at loww stress amplitudes, whereas the durability attained at higher amplitudes is practically the same.
Keywords in Czech
slitina AZ31, korozní napadení, iniciace únavových trhlin, cyklická deformační odezva
Keywords in English
alloy AZ31, corrosion attack, fatigue crack initiation, cyclic deformation response
RIV year
2011
Released
19.07.2011
Publisher
Chemické listy
Location
Novotného lávka 5 Praha 1
ISSN
0009-2770
Volume
105
Number
S
Pages from–to
787–789
Pages count
3
BIBTEX
@article{BUT75579,
author="Pavel {Doležal} and Josef {Zapletal} and Miroslava {Horynová} and Pavel {Gejdoš} and Ladislav {Čelko},
title="CYCLIC DEFORMATION RESPONSE OF AZ31 MAGNESIUM ALLOY AFTER CORROSION DEGRADATION",
year="2011",
volume="105",
number="S",
month="July",
pages="787--789",
publisher="Chemické listy",
address="Novotného lávka 5
Praha 1",
issn="0009-2770"
}