Výpočtové modelování porušování bi-materiálového rozhraní pryž -ocel

Computational Modelling of Bimaterial Interface Failure in View of Rubber-Steel Interface

journal article - other

en

This paper presents a brief review of selected approaches used for computational modelling of bimaterial interface failure and for evaluation of interface failure resistance. Attention is paid to the approaches that assume absence of initial interface crack. The applicability of such approaches to rubber-steel interface failure evaluation is discussed in the paper. The approach based on the so called cohesive zone model is preferred and demonstrated by an example of computational modelling of rubber-steel interface failure during a peel-test. The results of peel-test computational modelling are presented. The influence of cohesive zone element number on the results is also analysed. The results are consistent with experimental data.

Článek obsahuje stručné shrnutí přístupů k výpočtovému modelování porušování materiálového rozhraní. Pozornost je zaměřena na přístupy nevyžadující uvažování počáteční trhliny. Přístup použitý pro rozhraní pryž-ocel je založen na tzv. modelu kohezní zóny a je demonstrován na příkladu porušování tohoto rozhraní v průběhu odtrhávací zkoušky. Jsou prezentovány výsledky výpočtového modelování této zkoušky. Je analyzován vliv počtu kohezních prvků. Výsledky jsou v souladu s experimentálními daty.

This paper presents a brief review of selected approaches used for computational modelling of bimaterial interface failure and for evaluation of interface failure resistance. Attention is paid to the approaches that assume absence of initial interface crack. The applicability of such approaches to rubber-steel interface failure evaluation is discussed in the paper. The approach based on the so called cohesive zone model is preferred and demonstrated by an example of computational modelling of rubber-steel interface failure during a peel-test. The results of peel-test computational modelling are presented. The influence of cohesive zone element number on the results is also analysed. The results are consistent with experimental data.

výpočtové modelování, porušování rozhraní, bi-materiálové rozhraní, adhezní pevnost, model kohezní zóny, odtrhávací zkouška, pryž

computational modelling, interface failure, bimaterial interface, adhesion strength, cohesive zone model, peel-test, rubber