Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC

SMÉKALOVÁ, J. POSPÍŠILOVÁ, S. OBRTLÍK, K. JULIŠ, M. PODRÁBSKÝ, T.

Czech title

Iniciace a šíření únavových trhlin v materiálu inconel 713LC bez vrstvy a s vrstvou při teplotě 800 stC

English title

Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC

Type

journal article - other

Language

en

Original abstract

Fatigue crack initiation and propagation was studied in cast polycrystalline nickel base superalloy Inconel 713LC in as-received condition and with surface treatment by AlSi protective coating. Cylindrical specimens were cyclically strained under strain control with constant total strain amplitude at 800 ?C. Fatigue fracture surface, specimen surface, and specimen sections were investigated using optical microscopy and scanning electron microscopy. Fatigue crack initiation sites and fatigue crack growth mechanisms were identified and crack propagation rates were obtained base on striation spacing in fracture surfaces. The crack initiation mechanism study revealed reasons for the fatigue life increase in the surface treated material.

Czech abstract

Tato práce je zaměřena na studium iniciace a šíření únavových trhlin u lité polykrystalické niklové superslitiny Inconel 713LC jak s ochrannou povrchovou vrstvou na bázi AlSi, tak bez vrstvy při teplotě 800 ?C. Válcová zkušební tělesa byla cyklicky zatěžována za podmínek řízené deformace s konstantní amplitudou celkové deformace. Užitím optické a rastrovací elektronové mikroskopie byly analyzovány lomové plochy, povrch zatěžovaných vzorků a jejich osové řezy. Byla identifikována místa iniciace únavových trhlin a způsob jejich šíření a byla stanovena rychlost šíření na základě rozteče striací na lomových plochách. Studium mechanismu iniciace únavových trhlin odhalilo příčiny prodloužení únavové životnosti v materiálu s povrchovou úpravou.

English abstract

Fatigue crack initiation and propagation was studied in cast polycrystalline nickel base superalloy Inconel 713LC in as-received condition and with surface treatment by AlSi protective coating. Cylindrical specimens were cyclically strained under strain control with constant total strain amplitude at 800 ?C. Fatigue fracture surface, specimen surface, and specimen sections were investigated using optical microscopy and scanning electron microscopy. Fatigue crack initiation sites and fatigue crack growth mechanisms were identified and crack propagation rates were obtained base on striation spacing in fracture surfaces. The crack initiation mechanism study revealed reasons for the fatigue life increase in the surface treated material.

Keywords in Czech

iniciace, šíření únavové trhliny, rychlost šíření, fraktografie, striace

Keywords in English

initiation, fatigue crack propagation, crack propagation rate, fractography, striation

RIV year

2010

Released

01.12.2010

Publisher

VŠB Ostrava

Location

Ostrava

ISSN

1210-0471

Journal

Transaction of the VŠB-Technical university of Ostrava, Mechanical series

Volume

LVI

Number

2

Pages from–to

155–162

Pages count

8

BIBTEX


@article{BUT50304,
  author="Jana {Smékalová} and Simona {Hutařová} and Karel {Obrtlík} and Martin {Juliš} and Tomáš {Podrábský},
  title="Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC",
  journal="Transaction of the VŠB-Technical university of Ostrava, Mechanical series",
  year="2010",
  volume="LVI",
  number="2",
  month="December",
  pages="155--162",
  publisher="VŠB Ostrava",
  address="Ostrava",
  issn="1210-0471"
}