Publication detail

Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C

ZLÁMAL, B. FORET, R. BURŠÍK, J. SVOBODA, M.

Czech title

Stabilita mikrostruktury heterogenních svarových spojů žáropevných ocelí se zvýšeným obsahem dusíku při 500-900 st. C

English title

Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C

Type

journal article - other

Language

en

Original abstract

The dissimilar laboratory welds of bainitic T25 steel, currently being developed, and modified martensitic chromium P91 steel have been subject of study. Both base materials were ion-nitrided and homogenized at 1050 st.C/24h before welding. The redistribution of interstitials (C, N) and phase profiles in the weld joints were simulated using DICTRA software package at different annealing conditions of 600 st.C/240h and 900 st./18h. The results from the simulation were compared with experimental observations. A relatively good agreement between the simulation and the experiments was observed

Czech abstract

Předmětem našeho studia je heterogenní svarový spoj nově vyvíjené bainitické oceli T25 s modifikovanou martenzitickou chromovou ocelí P91. Oba základní materiály byly před svařením iontově nitridovány a následně homogenizovány při 1050 st.C/24h. Pomocí programu DICTRA byly provedeny simulace rozdělení intersticiálních prvků (uhlíku a dusíku) a fázových profilů ve svarovém spoji při podmínkách žíhání 600 st.C/240h a 900 st.C/18h. Vypočtené závislosti byly porovnány s experimentálně získanými výsledky. Výsledky počítačové simulace jsou ve velmi dobré shodě s experimentem.

English abstract

The dissimilar laboratory welds of bainitic T25 steel, currently being developed, and modified martensitic chromium P91 steel have been subject of study. Both base materials were ion-nitrided and homogenized at 1050 st.C/24h before welding. The redistribution of interstitials (C, N) and phase profiles in the weld joints were simulated using DICTRA software package at different annealing conditions of 600 st.C/240h and 900 st./18h. The results from the simulation were compared with experimental observations. A relatively good agreement between the simulation and the experiments was observed

Keywords in Czech

žáropevné oceli; svarové spoje;struktuení rozbory; termodynamické a kinetické modelování; redistribuce uhlíku a dusíku

Keywords in English

creep-resistant steel; weld joints; structural analyses; thermodynamic and kinetic modelling; carbon and nitrogen redistribution

RIV year

2007

Released

21.02.2007

ISSN

1012-0386

Journal

Defect and Diffusion Forum

Volume

263

Number

2

Pages from–to

195–200

Pages count

6

BIBTEX


@article{BUT44461,
  author="Bronislav {Zlámal} and Rudolf {Foret} and Jiří {Buršík} and Milan {Svoboda},
  title="Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Content at 500-900 st.C",
  journal="Defect and Diffusion Forum",
  year="2007",
  volume="263",
  number="2",
  month="February",
  pages="195--200",
  issn="1012-0386"
}