Publication detail
Low cycle fatigue of ductile cast iron with 2.8 % nickel
TESAŘOVÁ, H. PETRENEC, M. PACAL, B. MUSILOVÁ, I.
Czech title
Nízkocyklová únavová odolnost litiny s kuličkovým grafitem legované 2,8 % Ni
English title
Low cycle fatigue of ductile cast iron with 2.8 % nickel
Type
conference paper
Language
en
Original abstract
Cast ductile iron with the ferritic matrix alloying with 2,8% Ni was subjected to cycling with constant strain amplitudes and the cyclic stress-strain response and fatigue life were studied experimentally. The original microstructure is documented using light microscope. Fracture surface was studied using scanning electron microscopy. Manson-Coffin and Basquin laws can reasonably approximate the fatigue life data. Fatigue crack initiation from shrinkage cavity is documented.
Czech abstract
Zkoušky nízkocyklové únavy byly provedeny na válcových vzorcích z litiny s kuličkovým grafitem (dále LKG) v režimu řízené deformace za účelem posouzení únavové odolnosti. Byly získány křivky cyklického zpevnění, cyklická deformační křivka a křivky únavové životnosti. Je dokumentována mikrostruktura pomocí světelné mikroskopie. Lomová plocha byla pozorována pomocí elektronové rastrovací mikroskopie. Únavovou životnost lze uspokojivě charakterizovat Manson-Coffinovým a Basquinovým zákonem. Místa iniciace únavových trhlin v blízkosti povrchu jsou zdokumentovány.
English abstract
Cast ductile iron with the ferritic matrix alloying with 2,8% Ni was subjected to cycling with constant strain amplitudes and the cyclic stress-strain response and fatigue life were studied experimentally. The original microstructure is documented using light microscope. Fracture surface was studied using scanning electron microscopy. Manson-Coffin and Basquin laws can reasonably approximate the fatigue life data. Fatigue crack initiation from shrinkage cavity is documented.
Keywords in Czech
nízkocyklová únavová odolnost, litina s kuličkovým grafitem, Ni
Keywords in English
low cycle fatigue, ductile cast iron, alloying Ni
RIV year
2008
Released
13.05.2008
Publisher
Brno University of Technology
Location
Brno
ISBN
978-80-214-3646-6
Book
CD rom
Edition number
-
Pages from–to
39–39
Pages count
7
BIBTEX
@inproceedings{BUT25891,
author="Hana {Tesařová} and Martin {Petrenec} and Bohumil {Pacal} and Iveta {Musilová},
title="Low cycle fatigue of ductile cast iron with 2.8 % nickel",
booktitle="CD rom",
year="2008",
month="May",
pages="39--39",
publisher="Brno University of Technology",
address="Brno",
isbn="978-80-214-3646-6"
}