Original abstract
Nanocrystalline pure nickel and its particle-reinforced nanocomposite were produced by electrodeposition onto copper substrate under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain freestanding samples for the creep testing. The subject of study has been the evaluation of the creep characteristics of the electrodeposited unreinforced nickel and its nanocomposite reinforced by nano-sized SiO2 particles at temperatures in the range from 293 to 573 K. Fracture surfaces of the pure Ni and the composite after creep deformation were studied using SEM PHILIPS XL 30.
Czech abstract
Nanostrukturní čistý nikl a jeho nanokompozit byly připraveny elektrolytickým pokovováním na měděném substrátu za těchto podmínek:stejnosměrný proud 25mA, 30hod. Měděná podložka byla mechanicky odstraněna a tím byl získán experimentální materiál pro mechanické a creepové zkoušky. Předmětem studia bylo srovnání tahových a creepových vlastností elektrolyticky nanášeného čistého niklu a jeho kompozitu s nanometrickými částicemi SiO2. Creepové zkoušky byly provedeny v rozsahu teplot od 293K do 473K. Experimentální materiál (Ni a Ni+SiO2) byl studován pomocí REM a TEM. Studium bylo především zaměřeno na rozložení částic SiO2 v matrici a velikost zrn matrice i částic.
English abstract
Nanocrystalline pure nickel and its particle-reinforced nanocomposite were produced by electrodeposition onto copper substrate under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain freestanding samples for the creep testing. The subject of study has been the evaluation of the creep characteristics of the electrodeposited unreinforced nickel and its nanocomposite reinforced by nano-sized SiO2 particles at temperatures in the range from 293 to 573 K. Fracture surfaces of the pure Ni and the composite after creep deformation were studied using SEM PHILIPS XL 30.
Keywords in English
nickel, nanomaterial, creep
RIV year
2006
Released
01.11.2006
Publisher
VUT FSI v Brně
Location
Brno
ISBN
80-214-3331-0
Book
Nano 06
Edition number
1
Pages from–to
277–280
Pages count
4
BIBTEX
@inproceedings{BUT21669,
author="Petra {Cihlářová} and Jiří {Švejcar},
title="Creep testing of electrodeposited nickel and its particle-reinforced nanocomposite",
booktitle="Nano 06",
year="2006",
month="November",
pages="277--280",
publisher="VUT FSI v Brně",
address="Brno",
isbn="80-214-3331-0"
}