Vyhodnocování kumulace poškození pro houževnaté materiály

Evaluation of damage accumulation for ductile materials

article in a collection out of WoS and Scopus

en

The damage accumulation is one of the issues of ductile fracture modelling. One of the potential methods for assessing the damage evolution may be the tracking of the change in Young’s modulus. This contribution presents three measuring approaches to following the decrease of Young’s modulus, which is related to the damage progression. Simple loading-unloading technique was compared to the two approaches using the ultrasound. In one approach utilizing the ultrasound, the test was stopped for measuring the wave velocity, while no interruption was present during the other approach. The technique employing the ultrasound without stopping yielded rather scattered results with no trend observable. Nevertheless, the loading-unloading method resulted in greater degradation of Young’s modulus than in the techniques which applied the ultrasound.

Kumulace poškození je jedním z problémů modelování tvárného porušování. Jednou z potenciálních metod pro vyhodnocení vývoje poškození může být sledování změny Youngova modulu. Tento příspěvek prezentuje tři přístupy k měření pro sledování poklesu Youngova modulu, který je spojený s postupem poškození. Jednoduchá technika zatěžování-odtěžování byla porovnána s dvěma přístupy využívajícími ultrazvuk. V jednom přístupu využívajícím ultrazvuk byl test zastavován pro měření rychlosti vlny, zatímco během dalšího přístupu nebylo přítomno žádné přerušování. Technika používající ultrazvuk bez zastavování vedla spíše k výsledkům s velkým rozptylem s žádným pozorovatelným trendem. Metoda zatěžování-odtěžování nicméně vyústila ve větší degradaci Youngova modulu než při technice, která aplikovala ultrazvuk.

The damage accumulation is one of the issues of ductile fracture modelling. One of the potential methods for assessing the damage evolution may be the tracking of the change in Young’s modulus. This contribution presents three measuring approaches to following the decrease of Young’s modulus, which is related to the damage progression. Simple loading-unloading technique was compared to the two approaches using the ultrasound. In one approach utilizing the ultrasound, the test was stopped for measuring the wave velocity, while no interruption was present during the other approach. The technique employing the ultrasound without stopping yielded rather scattered results with no trend observable. Nevertheless, the loading-unloading method resulted in greater degradation of Young’s modulus than in the techniques which applied the ultrasound.

Polo-cyklický; porušení; plasticita; změkčení materiálu; nelineární kumulace poškození

Semi-cyclic; failure; plasticity; material weakening; non-linear damage accumulation