High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy
ŠULÁK, I. OBRTLÍK, K. ČELKO, L.
Czech title
High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy
English title
High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy
Type
journal article in Scopus
Language
en
Original abstract
The present work is focused on the study of low cycle fatigue behavior of grit blasted nickel-base superalloy Inconel 713LC (IN 713LC). Grit blasting parameters are obtained. Button end specimens of IN 713LC in as-received condition and with grit blasted surface were fatigued under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Both materials exhibit the same stress-strain response. It has not been observed any improvement or reduction of low cycle fatigue life in representation of total strain amplitude versus number of cycles to failure of grit blasted material in comparison with as-received material. Surface relief and fracture surface were observed in SEM. The little effect of surface treatment on fatigue characteristics is discussed.
Czech abstract
The present work is focused on the study of low cycle fatigue behavior of grit blasted nickel-base superalloy Inconel 713LC (IN 713LC). Grit blasting parameters are obtained. Button end specimens of IN 713LC in as-received condition and with grit blasted surface were fatigued under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Both materials exhibit the same stress-strain response. It has not been observed any improvement or reduction of low cycle fatigue life in representation of total strain amplitude versus number of cycles to failure of grit blasted material in comparison with as-received material. Surface relief and fracture surface were observed in SEM. The little effect of surface treatment on fatigue characteristics is discussed.
English abstract
The present work is focused on the study of low cycle fatigue behavior of grit blasted nickel-base superalloy Inconel 713LC (IN 713LC). Grit blasting parameters are obtained. Button end specimens of IN 713LC in as-received condition and with grit blasted surface were fatigued under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Both materials exhibit the same stress-strain response. It has not been observed any improvement or reduction of low cycle fatigue life in representation of total strain amplitude versus number of cycles to failure of grit blasted material in comparison with as-received material. Surface relief and fracture surface were observed in SEM. The little effect of surface treatment on fatigue characteristics is discussed.
Keywords in English
Grit blasting, fatigue life, cyclic stress-strain response, high temperature fatigue, IN 713LC
RIV year
2015
Released
21.09.2015
Publisher
Trans Tech Publications
Location
Switzerland
ISSN
1013-9826
Volume
665
Number
2016
Pages from–to
73–76
Pages count
4
BIBTEX
@article{BUT117340,
author="Ivo {Šulák} and Karel {Obrtlík} and Ladislav {Čelko},
title="High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy",
year="2015",
volume="665",
number="2016",
month="September",
pages="73--76",
publisher="Trans Tech Publications",
address="Switzerland",
issn="1013-9826"
}