Studium deformace povlaku u plechů pomocí tahové zkoušky

Study of deformation coating for sheets by using tensile test

journal article - other

en

This article focuses on the study of the defined values of tensile strain and the effect of low temperature plasma adhesion selected coatings on steel samples using a tensile testing flat test bars. Samples were made by machining and welding technologies. The flat test bars were tested by pulling on a test rig UPC 1200. Part of the samples were treated on the surface prior to coating by a tensile test, second base coat and with a final coat continuous multi plasma system. The selected test samples were determined from the tensile test of the material characteristics, such as e.g. the yield strength Rp0,2, tensile strength Rm is, an elongation A50, Ag apparent from the tensile diagrams see. table.1.

Článek je zaměřen na studium definovaných hodnot deformace v tahu . u zvoleného povlaku s využitím tahové zkoušky u plochých zkušebních tyčí vyrobených technologií obráběním a svařováním. Ploché zkušební tyče byly testovány tahem na zkušebním zařízení typu UPC 1200. Část vzorků na povrchu byla ošetřena průběžně multitryskovým plazmovým systémem před tahovou zkouškou ocelových vzorků bez povlaku a ostatní s nanesením povlaků jednak základního laku, tak i finálního laku. Na vybraných zkušebních vzorcích byly zjištěny z tahové zkoušky materiálové charakteristiky, jako je mez kluzu Rp0,2, mez pevnosti v tahu je Rm a odpovídající hodnoty deformace v tahu . zřejmé z tahových diagramů.

This article focuses on the study of the defined values of tensile strain and the effect of low temperature plasma adhesion selected coatings on steel samples using a tensile testing flat test bars. Samples were made by machining and welding technologies. The flat test bars were tested by pulling on a test rig UPC 1200. Part of the samples were treated on the surface prior to coating by a tensile test, second base coat and with a final coat continuous multi plasma system. The selected test samples were determined from the tensile test of the material characteristics, such as e.g. the yield strength Rp0,2, tensile strength Rm is, an elongation A50, Ag apparent from the tensile diagrams see. table.1.

Tahová zkouška, plech s povlakem, přilnavost povlaku, multitryskový plazmový systémem

Tensile test, sheet with coating, adhesion of coating, multi-jet plasma system