VLIV POVLAKU ALTICRN PRO FRÉZOVÁNÍ OCELI 1.8159 BEZ POUŽITÍ PROCESNÍ KAPALINY

JAROŠ, A. FIALA, Z. DVOŘÁČEK, J.

Český název

VLIV POVLAKU ALTICRN PRO FRÉZOVÁNÍ OCELI 1.8159 BEZ POUŽITÍ PROCESNÍ KAPALINY

Anglický název

INVESTIGATION OF THE INFLUENCE OF ALTICRN COATING FOR DRY MILLING OF CONSTRUCTION STEEL 1.8159

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

This study deals with the benefits of very hard PVD coatings applied to the tools of high speed steels. The coating was synthesized by a cathodic-arc deposition process (CAE). The milling was carried out without using process liquid, so it was dry machining. During testing, cutting speed was varied (30; 35 and 40 m/min), but the feed per tooth (0.05 mm) and depth of cut (2 mm) were constant. The cutting tests were performed on vertical milling machine FV 25 CNC. The aim of this experiment was to compare the coated and uncoated HSSE-PM end mills and find out the benefits of coating AlTiCrN. The monitored parameters were force loading and flank wear. Best results were achieved by machining cutting speed 35m/min. Tools with PVD coating AlTiCrN had ten times longer durability than uncoated tools.

Český abstrakt

Příspěvek pojednává o výhodách velmi tvrdých PVD povlaků používaných na nástroje z rychlořezných ocelí. Testovaným povlakem byl PVD povlak AlTiCrN, který byl na nástroj nanesen odpařováním pomocí elektrického oblouku. Povlaky na bázi Al se běžně používají pro frézování bez použití procesní kapaliny. Cílem experimentu bylo porovnání silového zatížení a opotřebení hřbetu u povlakovaných a nepovlakovaných HSS-PM fréz. Experiment probíhal na vertikální frézce FV 25 CNC. Po celou dobu experimentu byla konstantní šířka záběru ostří (2mm) a posuv na zub (0,05mm), proměnným vstupním parametrem byla pouze řezná rychlost (30; 35 a 40 m/min). Nejlepších výsledků bylo dosaženo při řezné rychlosti 35m/min, kde nástroj s AlTiCrN povlakem vydržel desetkrát více než nepovlakovaný nástroj (kritérium opotřebení VB=0,2mm).

Anglický abstrakt

This study deals with the benefits of very hard PVD coatings applied to the tools of high speed steels. The coating was synthesized by a cathodic-arc deposition process (CAE). The milling was carried out without using process liquid, so it was dry machining. During testing, cutting speed was varied (30; 35 and 40 m/min), but the feed per tooth (0.05 mm) and depth of cut (2 mm) were constant. The cutting tests were performed on vertical milling machine FV 25 CNC. The aim of this experiment was to compare the coated and uncoated HSSE-PM end mills and find out the benefits of coating AlTiCrN. The monitored parameters were force loading and flank wear. Best results were achieved by machining cutting speed 35m/min. Tools with PVD coating AlTiCrN had ten times longer durability than uncoated tools.

Klíčová slova česky

sílové zatížení, opotřebení hřbetu, rychlořezná ocel, PVD povlaky, čelní frézování

Klíčová slova anglicky

force loading, flank wear, high-speed steel, PVD coatings, face milling

Rok RIV

2012

Vydáno

17.12.2012

Nakladatel

MAGNANIMITAS

Místo

Hradec Králové

ISBN

978-80-905243-3-0

Kniha

Sborník příspěvků Mezinárodní Masarykovy konference pro doktorandy a mladé vědecké pracovníky 2012

Číslo edice

3

Strany od–do

3475–3482

Počet stran

7

BIBTEX


@inproceedings{BUT96579,
  author="Aleš {Jaroš} and Zdeněk {Fiala} and Jan {Dvořáček},
  title="INVESTIGATION OF THE INFLUENCE OF ALTICRN COATING FOR DRY MILLING OF CONSTRUCTION STEEL 1.8159",
  booktitle="Sborník příspěvků Mezinárodní Masarykovy konference pro doktorandy a mladé vědecké pracovníky 2012",
  year="2012",
  month="December",
  pages="3475--3482",
  publisher="MAGNANIMITAS",
  address="Hradec Králové",
  isbn="978-80-905243-3-0"
}