Vliv plazmaticky naneseného AlSi povlaku na nízkocyklové únavové vlastnosti lité slitiny Inconel 738LC
OBRTLÍK, K. HUTAŘOVÁ, S. JULIŠ, M. ČELKO, L. PODRÁBSKÝ, T.
Český název
Vliv plazmaticky naneseného AlSi povlaku na nízkocyklové únavové vlastnosti lité slitiny Inconel 738LC
Anglický název
Effect of Plasma sprayed AlSi coating on low cycle fatigue properties of cast superalloy Inconel 738LC
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
Air plasma spraying was applied to obtain AlSi protective surface coating on cylindrical specimens of cast polycrystalline superalloy Inconel 738LC. Chemical composition of the surface treated layer was studied and the hardness depth profile was measured. Surface treated and untreated specimens were cyclically strained under total strain control at 800 degC in air. Cyclic stress-strain response and fatigue life of both materials were obtained. The coating results in a slight decrease of cyclic stress-strain curve. A detrimental effect of the surface treatment on derived Wöhler curve is documented while Manson-Coffin curves of both materials are almost identical. Specimen section observations and fracture surface examinations help to discuss fatigue behaviour of both materials.
Český abstrakt
Na povrch válcových zkušebních těles z lité niklové superslitiny Inconel 738LC byl nanesen povlak AlSi pomocí plazmatické depozice, metodou APS. V příspěvku byla studována struktura a chemické složení povlaku, spolu s tvrdostí v závislosti na vzdálenosti od povrchu. Zkušební tělesa s AlSi povlakem a bez povlaku byla cyklicky zatěžována v režimu řízení deformace při teplotě 800 C na vzduchu. V příspěvku jsou uvedeny křivky cyklického zpevnění a změkčení a křivky únavové životnosti. Zatímco Manson-Coffinovy křivky životnosti povlakovaných a nepovlakovaných zkušebních těles jsou téměř totožné, v případě derivovaných Wöhlerových křivek životnosti lze konstatovat, že povlak AlSi má negativní vliv na cyklickou životnost materiálu. Dále je v příspěvku uveden fraktografický rozbor lomových ploch.
Anglický abstrakt
Air plasma spraying was applied to obtain AlSi protective surface coating on cylindrical specimens of cast polycrystalline superalloy Inconel 738LC. Chemical composition of the surface treated layer was studied and the hardness depth profile was measured. Surface treated and untreated specimens were cyclically strained under total strain control at 800 degC in air. Cyclic stress-strain response and fatigue life of both materials were obtained. The coating results in a slight decrease of cyclic stress-strain curve. A detrimental effect of the surface treatment on derived Wöhler curve is documented while Manson-Coffin curves of both materials are almost identical. Specimen section observations and fracture surface examinations help to discuss fatigue behaviour of both materials.
Klíčová slova česky
Vysokoteplotní únava, Inconel 738LC, křivky únavové životnosti, závislost napětí-deformace, plazmatický povlak AlSi
Klíčová slova anglicky
High temperature fatigue, Inconel 738LC, fatigue life curves, cyclic stress-strain curve, AlSi plasma coating
Rok RIV
2012
Vydáno
25.05.2012
Nakladatel
TANGER Ltd.
Místo
Ostrava
ISBN
978-80-87294-29-1
Kniha
METAL 2012 Conference proceedings
Číslo edice
1
Strany od–do
1013–1018
Počet stran
6
BIBTEX
@inproceedings{BUT94096,
author="Karel {Obrtlík} and Simona {Hutařová} and Martin {Juliš} and Ladislav {Čelko} and Tomáš {Podrábský},
title="Effect of Plasma sprayed AlSi coating on low cycle fatigue properties of cast superalloy Inconel 738LC",
booktitle="METAL 2012 Conference proceedings",
year="2012",
month="May",
pages="1013--1018",
publisher="TANGER Ltd.",
address="Ostrava",
isbn="978-80-87294-29-1"
}