Stanovení kritické geometrie trhliny na bimateriálovém rozhraní
ŠEVČÍK, M. ZOUHAR, M. MÁŠA, B. HUTAŘ, P. NÁHLÍK, L.
Český název
Stanovení kritické geometrie trhliny na bimateriálovém rozhraní
Anglický název
On a critical geometry of a crack arrested at a bimaterail interface
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
Surface crack propagation in a thin soft protective layer on a massive stiffer substrate is analyzed using generalized linear elastic fracture mechanics. The growth of the initial crack is considered in both forward and sideways directions and the influence of the interface between the protective layer and massive substrate on the final crack configuration is investigated. It is shown that, depending on the elastic mismatch, the part of the crack front can be arrested at the interface protective layer/substrate and the rest of the crack grows continuously sideways only. The effective value of the stress intensity factor is used in order to predict the conditions under which the crack will propagate through the interface into the second material. Corresponding calculations have been made by finite element method.
Český abstrakt
Za pomoci zobecněné lomové mechaniky je analyzována trhlina rostoucí v tenké poddajné ochranné vrstvě, která je nanesena na masivním tužším podkladě. Růst počáteční trhliny je uvažován v obou směrech a je zjišťován vliv rozhraní mezi ochannou vrstvou a podkladem na finální konfiguraci zkoumané trhliny. Je ukázáno, že v závislosti na elastické rozdílnosti obou materiálů může být část čela trhliny zastavena na rozhraní materiálů a zbytek trhliny pokračuje v růstu pouze do boků. Efektivní hodnota součinitele intenzity napětí je použita k predicky podmínek, za jakých trhlina protoste skrz rozhraní do druhého materiálu. Náležité výpočty byly provedeny metodou konečných prvků.
Anglický abstrakt
Surface crack propagation in a thin soft protective layer on a massive stiffer substrate is analyzed using generalized linear elastic fracture mechanics. The growth of the initial crack is considered in both forward and sideways directions and the influence of the interface between the protective layer and massive substrate on the final crack configuration is investigated. It is shown that, depending on the elastic mismatch, the part of the crack front can be arrested at the interface protective layer/substrate and the rest of the crack grows continuously sideways only. The effective value of the stress intensity factor is used in order to predict the conditions under which the crack will propagate through the interface into the second material. Corresponding calculations have been made by finite element method.
Klíčová slova česky
lomová mechanika na rozhraní, zobecněný faktor intenzity napětí, trhlina
Klíčová slova anglicky
fracture mechanics of an interface, generalized stress intensity factor, crack
Rok RIV
2012
Vydáno
30.08.2012
Nakladatel
Západočeská univerzita v Plzni
Místo
Plzeň
ISBN
978-80-261-0097-3
Kniha
Conference Proceedings of the 14th International Conference APPLIED MECHANICS
Strany od–do
1–4
Počet stran
4
BIBTEX
@inproceedings{BUT93489,
author="Martin {Ševčík} and Michal {Zouhar} and Bohuslav {Máša} and Pavel {Hutař} and Luboš {Náhlík},
title="On a critical geometry of a crack arrested at a bimaterail interface",
booktitle="Conference Proceedings of the 14th International Conference APPLIED MECHANICS",
year="2012",
month="August",
pages="1--4",
publisher="Západočeská univerzita v Plzni",
address="Plzeň",
isbn="978-80-261-0097-3"
}