Aplikace PVD povlaků pro obrábění složitých tvarových ploch

On the Application of the PVD Hard Coatings for Ball Milling of Shaped Surfaces

článek v časopise - ostatní, Jost

en

Force load analysis is a usual procedure of current cutting tool testing in not only ball end milling but in general machining. This paper is aimed to force load analysis of the cutting tool when the HSS ball end milling is performed onto an alumina alloy. A variation of the cutting tool force loading has been observed when a tilt of the tool was set perpendicularly to the direction of the feed speed vector in the range 0-20deg and cutting conditions were kept constant. In the first part of the study, some uncoated HSS ball milling tools have been used to exclude an influence of PVD coating and its disperse in quality. In the second part of the project the PVD coatings on the base of (TixAl1-x)N and TiB2 have been successively applied. However, the main objective of the research was to quantify other cutting phenomena also, like the chip formation, roughness of the machined surface as they present a key role in the complex surface machining for moulds.

Analýza silového zatížení je běžnou součástí současného testování nástrojů, a to nejen pro testování nástrojů s kulovým čelem, ale obecně celého obrábění. Tento článek je zaměřen na analýzu silového zatížení při obrábění hliníkové slitiny frézou s kulovým čelem vyrobené z HSS. Při naklopení nástroje ve směru kolmém ke směru posuvu v rozsahu od 0 do 20deg byly pozorovány rozdíly silového zatížení. Řezné podmínky byly v průběhu obrábění nezměněny. V první části byl použit nepovlakovaný nástroj pro vyloučení vlivu povlaku a rozptylu v jeho kvalitě. V druhé části byly použity nástroje s povlaky na bázi (TixAl1-x)N a TiB2, přičemž bylo dosaženo zajímavých výsledků. Mimo jiné byly zkoumány parametry jako utváření třísky, drsnost povrchu a další, protože hrají klíčovou roli při obrábění tvarově složitých součástí pro formy.

Force load analysis is a usual procedure of current cutting tool testing in not only ball end milling but in general machining. This paper is aimed to force load analysis of the cutting tool when the HSS ball end milling is performed onto an alumina alloy. A variation of the cutting tool force loading has been observed when a tilt of the tool was set perpendicularly to the direction of the feed speed vector in the range 0-20deg and cutting conditions were kept constant. In the first part of the study, some uncoated HSS ball milling tools have been used to exclude an influence of PVD coating and its disperse in quality. In the second part of the project the PVD coatings on the base of (TixAl1-x)N and TiB2 have been successively applied. However, the main objective of the research was to quantify other cutting phenomena also, like the chip formation, roughness of the machined surface as they present a key role in the complex surface machining for moulds.

tvarové obrábění, silové zatížení, drsnost povrchu, PVD povlak

ball milling, forces, roughness, PVD coating