Detail publikace
Stabilita MR efektu v průběhu dlouhodobého zatěžování
ROUPEC, J. MAZŮREK, I.
Český název
Stabilita MR efektu v průběhu dlouhodobého zatěžování
Anglický název
Stability of magnetorheological effect during long term operation
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
The article describes a determination of stability of magnetorheological (MR) effect during long term operation. The operation carried out in a cus-tom design rheometer, which is built in a mechanical pulsator. The rheom-eter design allows measurement of the rheological properties of MR fluid and its exposure to a long-term loading simultaneously, without any ma-nipulation of the measured sample. The operation ran under conditions which correspond to real conditions in the automotive MR damper. The results of long term operation show that during the durability test an yield stress increased up to five times in off-state due to in-use-thickening (IUT). The same increase was identified in on-state. These results disprove a hy-pothesis that a measurable decreasing of MR effect due to the degradation of magnetic properties arises during the long term operation.
Český abstrakt
Článek popisuje určení stability magnetoreologického (MR) efektu během dlouhodobého zatěžování. Zatěžování probíhalo na slit-flow reometru vlastní konstrukce, který je zabudován v mechanickém pulzátoru. Kon-strukce reometru umožňuje zároveň měřit reologické vlastnosti MR kapa-liny a zároveň ji podrobovat dlouhodobému zatěžování, aniž by došlo k manipulaci s měřeným vzorkem. Zatěžování probíhá za podmínek, které odpovídají reálným podmínkám v automobilovém MR tlumiči. Výsledky dlouhodobého zatěžování ukazují, že v průběhu testu došlo až k pětinásob-nému navýšení meze kluzu v neaktivovaném stavu vlivem provozního houstnutí. Stejné navýšení bylo identifikováno v aktivovaném stavu. Tyto výsledky vyvracejí hypotézu, že v průběhu dlouhodobého zatěžování do-chází k měřitelnému snižování MR efektu vlivem zhoršených magnetických vlastností částic.
Anglický abstrakt
The article describes a determination of stability of magnetorheological (MR) effect during long term operation. The operation carried out in a cus-tom design rheometer, which is built in a mechanical pulsator. The rheom-eter design allows measurement of the rheological properties of MR fluid and its exposure to a long-term loading simultaneously, without any ma-nipulation of the measured sample. The operation ran under conditions which correspond to real conditions in the automotive MR damper. The results of long term operation show that during the durability test an yield stress increased up to five times in off-state due to in-use-thickening (IUT). The same increase was identified in on-state. These results disprove a hy-pothesis that a measurable decreasing of MR effect due to the degradation of magnetic properties arises during the long term operation.
Klíčová slova česky
magnetoreologická kapalina, MR kapalina, mez kluzu, viskozita, LDE, dlouhodobé zatěžování
Klíčová slova anglicky
magnetorheological fluid, MR fluid, yield stress, viscosity, LDE, long-term operation
Rok RIV
2011
Vydáno
19.09.2011
Nakladatel
Springer-Verlag
Místo
Berlin Heidelberg
ISBN
978-3-642-23243-5
Kniha
Mechatronics
Strany od–do
561–567
Počet stran
7
BIBTEX
@inproceedings{BUT74066,
author="Jakub {Roupec} and Ivan {Mazůrek},
title="Stability of magnetorheological effect during long term operation",
booktitle="Mechatronics",
year="2011",
month="September",
pages="561--567",
publisher="Springer-Verlag",
address="Berlin Heidelberg",
isbn="978-3-642-23243-5"
}