Microfractography of Fish-Eye Fractures in Nitrided Steel
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
The paper presents results of the micro-fractographical study of fish-eye cracks that were formed in plasma-nitrided specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading regimes. Analysis of the local striation field found near the inclusion in the center of the fish-eye crack together with the local roughness measurements support the hypothesis that the cracks propagate predominantly by mode I micromechanisms. Moreover, the extrapolation of the local crack growth rate curve to the overall fish-eye crack region suggests that similarly to the gigacycle fatigue, the most of the fatigue life is spent on the initiation of the interior microcrack.
Český abstrakt
V článku jsou prezentovány výsledky mikrofraktografické analýzy trhlin typu "rybí oko", které vznikly v plasmově nitridovaných ocelových vzorcích v důsledku jejich experimentálního zatěžování ohybem, krutem a jejich synchronní soufázovou kombinací. Analýza lokálního pole striací situovaného v těsné blízkosti inkluze ve středu "rybího oka" společně s vyhodnocením parametrů lokální drsnosti ukazuje, že k šíření trhliny dochází primárně mikromechanismy zátěžného módu I. Extrapolace lokální rychlosti šíření na celou oblast "rybího oka" naznačuje, že dominantní etapou degradačního procesu je, podobně jako v případě gigacyklové únavy, iniciace vnitřní trhliny.
Anglický abstrakt
The paper presents results of the micro-fractographical study of fish-eye cracks that were formed in plasma-nitrided specimens under symmetrical bending, symmetrical torsion and biaxial in-phase bending-torsion loading regimes. Analysis of the local striation field found near the inclusion in the center of the fish-eye crack together with the local roughness measurements support the hypothesis that the cracks propagate predominantly by mode I micromechanisms. Moreover, the extrapolation of the local crack growth rate curve to the overall fish-eye crack region suggests that similarly to the gigacycle fatigue, the most of the fatigue life is spent on the initiation of the interior microcrack.
Klíčová slova česky
kvantitativní fraktografie, rybí oka, únava při ohybu a krutu, striace, nitridovaná ocel
Klíčová slova anglicky
Fractography, fish-eye cracks, bending-torsion fatigue, striations, nitrided steel
Rok RIV
2011
Vydáno
15.07.2011
Místo
Brno
ISSN
0009-2770
Ročník
105
Číslo
S
Strany od–do
721–724
Počet stran
4
BIBTEX
@article{BUT73471,
author="Karel {Slámečka} and Jaroslav {Pokluda} and Kateřina {Bonaventurová} and Ladislav {Čelko},
title="Microfractography of Fish-Eye Fractures in Nitrided Steel",
year="2011",
volume="105",
number="S",
month="July",
pages="721--724",
address="Brno",
issn="0009-2770"
}