Syntéza a charakterizace multikomponentního perovskitového systému založeného na La-Sr-Fe-Ti-O
BARTONÍČKOVÁ, E.
Český název
Syntéza a charakterizace multikomponentního perovskitového systému založeného na La-Sr-Fe-Ti-O
Anglický název
Synthesis and characterization of multicomponent perovskites based on La-Sr-Fe-Ti-O system
Typ
konferenční sborník (ne článek)
Jazyk
en
Originální abstrakt
Preparation of two types of perovskite system based on La – Sr – Fe – Ti – O and processing behavior (shaping, pressing and sintering) were studied within this work. The La1-xSrxFe1-yTiyO3-d (x = 0.8, y = 0.2 – 0.4) ceramics was synthesized by two wet chemical techniques – glycine/nitrate combustion reaction and spray pyrolysis method. XRD analysis of prepared powders showed single phase perovskite structure. The dense ceramic bodies in the shape of rectangular bars with relative bulk density in the range of 96 – 98 % were prepared by pressureless sintering at 1200C for 8 – 10 hours. The thermal expansion of sintered ceramic was studied by high temperature dilatometry. The coefficient of thermal expansion was determined in the range of 14.10-6 K-1- 31.10-6 K-1.
Český abstrakt
Tato práce se zabývá přípravou práškového perovskitového systému na bázi La – Sr – Fe – Ti – O o různé stechiometrii a určení chování při dálším zpracování (tvarování, lisování, slinování). Systémy La1-xSrxFe1-yTiyO3-? (x = 0.8, y = 0.2 – 0.4) byly připraveny pomocí dvou odlišných metod založených na tzv. mokré cestě – glycine/nitrate spalovací reakce a sprejová pyrolýza. RTG analýza připravených prášků ukázala fázovou čistotu připravené perovskitové fáze. Byla připravena hutná keramika o rozměrech (5x5x20)mm o teoretické hustotě v rozsahu 96-98%. Byla studována tepelná roztažnost připravených keramik a na základě experimetů byl stanoven koeficient tepelné roztažnosti.
Anglický abstrakt
Preparation of two types of perovskite system based on La – Sr – Fe – Ti – O and processing behavior (shaping, pressing and sintering) were studied within this work. The La1-xSrxFe1-yTiyO3-d (x = 0.8, y = 0.2 – 0.4) ceramics was synthesized by two wet chemical techniques – glycine/nitrate combustion reaction and spray pyrolysis method. XRD analysis of prepared powders showed single phase perovskite structure. The dense ceramic bodies in the shape of rectangular bars with relative bulk density in the range of 96 – 98 % were prepared by pressureless sintering at 1200C for 8 – 10 hours. The thermal expansion of sintered ceramic was studied by high temperature dilatometry. The coefficient of thermal expansion was determined in the range of 14.10-6 K-1- 31.10-6 K-1.
Klíčová slova česky
G/N spalovací syntéza, sprejová pyrolýza, perovskity
Klíčová slova anglicky
GNP process, spray pyrolysis, perovskites
Vydáno
31.01.2009
Nakladatel
Vysoké učení technické v Brně
Místo
Vysoké učení technické v Brně Fakulta strojního inženýrství, Technická 2, 616 69 Brno
ISBN
978-80-214-3834-7
Kniha
FSI Junior konference 2008
Strany od–do
64–69
Počet stran
6
BIBTEX
@proceedings{BUT65739,
author="Eva {Bartoníčková},
title="Synthesis and characterization of multicomponent perovskites based on La-Sr-Fe-Ti-O system",
booktitle="FSI Junior konference 2008",
year="2009",
month="January",
pages="64--69",
publisher="Vysoké učení technické v Brně",
address="Vysoké učení technické v Brně
Fakulta strojního inženýrství,
Technická 2, 616 69 Brno",
isbn="978-80-214-3834-7"
}