Study of Sintering of Oxide Ceramics at Constant Rate of Heating and by means of Rate-Controlled Sintering Method

MACA, K. HADRABA, H. CIHLÁŘ, J.

Anglický název

Study of Sintering of Oxide Ceramics at Constant Rate of Heating and by means of Rate-Controlled Sintering Method

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

The kinetics of sintering of ceramic materials based on alumina, zirconia, ZTA and ATZ was studied at a constant rate of heating and by means of the rate controlled sintering method. Ceramic samples were prepared by cold isostatic pressing and powder injection moulding. The sintering was performed in air atmosphere either in a high-temperature dilatometer or in a high-temperature superkanthal furnace. It was found that the alumina-based ceramics sintered at a higher temperature than those based on zirconia. The resultant relative densities were higher for the ceramics prepared by cold isostatic pressing then for those prepared by injection moulding. Slow rates of heating (2°C/min) were more convenient for reaching higher relative densities in the case of injection moulded ceramics. The maximum relative densities and flexural strength of ceramics were obtained at one hour’s delay at a temperature of 1500°C.

Anglický abstrakt

The kinetics of sintering of ceramic materials based on alumina, zirconia, ZTA and ATZ was studied at a constant rate of heating and by means of the rate controlled sintering method. Ceramic samples were prepared by cold isostatic pressing and powder injection moulding. The sintering was performed in air atmosphere either in a high-temperature dilatometer or in a high-temperature superkanthal furnace. It was found that the alumina-based ceramics sintered at a higher temperature than those based on zirconia. The resultant relative densities were higher for the ceramics prepared by cold isostatic pressing then for those prepared by injection moulding. Slow rates of heating (2°C/min) were more convenient for reaching higher relative densities in the case of injection moulded ceramics. The maximum relative densities and flexural strength of ceramics were obtained at one hour’s delay at a temperature of 1500°C.

Klíčová slova anglicky

ceramics, sintering, microstructure

Rok RIV

2002

Vydáno

01.01.2000

Nakladatel

WILEY-VCH Verlag Gmbh, Weinheim

Místo

Weinheim

ISBN

3-527-30194-1

Kniha

Ceramics-Processing, Reliability and Wear

Číslo edice

1

Počet stran

6

BIBTEX


@inproceedings{BUT6252,
  author="Karel {Maca} and Hynek {Hadraba} and Jaroslav {Cihlář},
  title="Study of Sintering of Oxide Ceramics at Constant Rate of Heating and by means of Rate-Controlled Sintering Method",
  booktitle="Ceramics-Processing, Reliability and Wear",
  year="2000",
  month="January",
  publisher="WILEY-VCH Verlag Gmbh, Weinheim",
  address="Weinheim",
  isbn="3-527-30194-1"
}