Oscilační vrásky a háky na povrchu continuálně litých bram a jejich vztah k průvalu
STRÁNSKÝ, K. KAVIČKA, F. SEKANINA, B. DOBROVSKÁ, J. ŠTĚTINA, J. MAUDER, T.
Český název
Oscilační vrásky a háky na povrchu continuálně litých bram a jejich vztah k průvalu
Anglický název
Oscillation Marks and Hooks on the Surface of Concast Slabs and their Relation to Breakout
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, this could lead to immediate interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. If the dimensionless analysis is applied for assessing and reducing the number of these parameters, then it is possible to express the level of risk of breakout as a function of five dimensionless criteria.
Český abstrakt
V sekundární zoně chlazení, kde se brama začíná narovnávat může vzniknout průval v místech chemické a teplotní heterogenity, zvyšování napětí a vysoké koncentrace nekovových, struskových vměstků. Zvláště v případě odlévání dvou taveb s různým chemickým složením bezprostředně za sebou může k průvalu dojít. Výše nebezpečí vzniku průvalu může být vyjádřena jako funkce pěti bezrozměrných kriterií.
Anglický abstrakt
In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, this could lead to immediate interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. If the dimensionless analysis is applied for assessing and reducing the number of these parameters, then it is possible to express the level of risk of breakout as a function of five dimensionless criteria.
Klíčová slova česky
kontinuáně lité bramy, oscilační vrásky, háky, chemické složení, průval, kriteria
Klíčová slova anglicky
concast slabs, oscillation marks, hooks, chemical composition, breakout, criteria
Rok RIV
2011
Vydáno
21.01.2011
Nakladatel
Trans Tech Publications Ltd
Místo
Zuerich, Switzerland
ISSN
1013-9826
Ročník
465
Číslo
1
Strany od–do
467–470
Počet stran
4
BIBTEX
@article{BUT51034,
author="Karel {Stránský} and František {Kavička} and Bohumil {Sekanina} and Jana {Dobrovská} and Josef {Štětina} and Tomáš {Mauder},
title="Oscillation Marks and Hooks on the Surface of Concast Slabs and their Relation to Breakout",
year="2011",
volume="465",
number="1",
month="January",
pages="467--470",
publisher="Trans Tech Publications Ltd",
address="Zuerich, Switzerland",
issn="1013-9826"
}