Hydrogen embrittlement induced in bearing steel by electric erosion

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

The subject of analysis was a spherical-roller bearing which had to be dividet into halves by using of electrospark erosion.On the cutting surfaces of the rings defects were found.On the basis of microfractographic analysis was possible to arrive at a definite assumption that this was one of clasical manifestation of hydrogen embrittlement(delayed fracture) resulting from the combined effect of hydrogenation of subsurface layers during electroerosion and residual stress

Český abstrakt

Analýza ložiska,u kterého se objevily při půlení kroužků elektrojiskrovým řezáním povrchové a podpovrchové vady..Mikrofraktografická analýza prokázala,že kombinací účinku navodíkování při řezání a zbytkové napjatosti po přdchozích operacích došlo ke vzniku vodíékové křehkosti(zpožděným lomům)

Anglický abstrakt

The subject of analysis was a spherical-roller bearing which had to be dividet into halves by using of electrospark erosion.On the cutting surfaces of the rings defects were found.On the basis of microfractographic analysis was possible to arrive at a definite assumption that this was one of clasical manifestation of hydrogen embrittlement(delayed fracture) resulting from the combined effect of hydrogenation of subsurface layers during electroerosion and residual stress

Klíčová slova česky

zpožděné lomy; elektrojiskrová koroze; ložiska

Klíčová slova anglicky

dealayed fractures; electrospark erosion; bearings

Rok RIV

2010

Vydáno

01.03.2010

Nakladatel

HF TU Košice

Místo

Košice,SR

ISSN

1335-1532

Časopis

Acta Metallurgica Slovaca

Ročník

1

Číslo

2H

Strany od–do

99–103

Počet stran

5

BIBTEX


@article{BUT50395,
  author="Jiří {Švejcar} and Rudolf {Foret},
  title="Hydrogen embrittlement induced in bearing steel by electric erosion",
  journal="Acta Metallurgica Slovaca",
  year="2010",
  volume="1",
  number="2H",
  month="March",
  pages="99--103",
  publisher="HF TU Košice",
  address="Košice,SR",
  issn="1335-1532"
}