Trojrozměrné modelování interkrystalického lomu
POKLUDA, J. ŠANDERA, P.
Český název
Trojrozměrné modelování interkrystalického lomu
Anglický název
Three-Dimensional Modelling of Intergranular Fracture
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
A computer based 3D model of stable intergranular crack is developed. It simulates experimental and practical conditions occuring in fatigue, brittle fracture and stress corrosion cracking cases. Creation of the intergranular crack is constructed according to some geometrically justified rules. This procedure reflects well the real damage process and allows us to quantify the geometrically induced crack tip shielding due to the branched crack fro
Anglický abstrakt
A computer based 3D model of stable intergranular crack is developed. It simulates experimental and practical conditions occuring in fatigue, brittle fracture and stress corrosion cracking cases. Creation of the intergranular crack is constructed according to some geometrically justified rules. This procedure reflects well the real damage process and allows us to quantify the geometrically induced crack tip shielding due to the branched crack fro
Klíčová slova anglicky
computer modelling, Voronoi tesselation, intergranular surface, crack branching
Rok RIV
1999
Vydáno
06.09.1999
Nakladatel
TU Košice
Místo
Herľany, Slovenská republika
ISBN
80-7099-43
Kniha
Physical Metallurgy and Fracture of Materials '99
Počet stran
4
BIBTEX
@inproceedings{BUT501,
author="Jaroslav {Pokluda} and Pavel {Šandera},
title="Three-Dimensional Modelling of Intergranular Fracture",
booktitle="Physical Metallurgy and Fracture of Materials '99",
year="1999",
month="September",
publisher="TU Košice",
address="Herľany, Slovenská republika",
isbn="80-7099-43"
}