VLAŠIC, F. MAZAL, P. LIŠKUTÍN, P.

Český název

Využití metody AE během vysokocyklové únavy hliníkové slitiny

Anglický název

APPLICATION OF ACOUSTIC EMISSION METHOD DURING HIGH CYCLE FATIGUE OF ALUMINIUM ALLOY

Typ

článek v časopise - ostatní, Jost

Jazyk

en

Originální abstrakt

This paper deals with evaluation of degradation processes, which occur at cyclic loading of samples of Al alloy EN AW-2017/T4. NDT procedure – acoustic emission (AE) method was used for detection of microstructure changes during stages of fatigue damage accumulation and micro-cracks initialisation. This measurement was completed with analysis of loading frequency changes of the fatigue test device. AE signal records obtained with use of the newly developed AE analyser with continual recording of signal are commented and showed other parameters of AE sample in detail.

Český abstrakt

Článek se zabývá možnostmi hodnocení degradačních procesů, které se objevují při cyklickém zatěžování zkušebních vzorků z Al slitiny EN AW-2017/T4. Pro detekci změn mikrostruktury v průběhu akumulace poškození a iniciace mikrotrhlin byla využita metoda akustické emise. Toto měření bylo doplněno analyzou změn zatěžovací frekvence zkušebního zařízení. Jsou ukázány a detailněji popsány další parmetry signalu AE, získané s pomocí nově vyvinutého analyzátoru IPL s kontinuálním záznamem a zpracováním signalu AE .

Anglický abstrakt

This paper deals with evaluation of degradation processes, which occur at cyclic loading of samples of Al alloy EN AW-2017/T4. NDT procedure – acoustic emission (AE) method was used for detection of microstructure changes during stages of fatigue damage accumulation and micro-cracks initialisation. This measurement was completed with analysis of loading frequency changes of the fatigue test device. AE signal records obtained with use of the newly developed AE analyser with continual recording of signal are commented and showed other parameters of AE sample in detail.

Klíčová slova česky

únava materiálu, akustická emise, trhlina, snímač

Klíčová slova anglicky

fatigue of materials, acoustic emission, crack, sensor

Rok RIV

2010

Vydáno

05.11.2010

Nakladatel

TU VSB Ostrava

Místo

Ostrava

ISSN

1210-0471

Časopis

Transaction of the VŠB-Technical university of Ostrava, Mechanical series

Ročník

56

Číslo

2

Strany od–do

187–196

Počet stran

10

BIBTEX


@article{BUT49959,
  author="František {Vlašic} and Pavel {Mazal} and Petr {Liškutín},
  title="APPLICATION OF ACOUSTIC EMISSION METHOD DURING HIGH CYCLE FATIGUE OF ALUMINIUM ALLOY",
  journal="Transaction of the VŠB-Technical university of Ostrava, Mechanical series",
  year="2010",
  volume="56",
  number="2",
  month="November",
  pages="187--196",
  publisher="TU VSB Ostrava",
  address="Ostrava",
  issn="1210-0471"
}