Šíření krátkých únavových trhlin v hliníkové slitině EN AW-6082/T6
LIŠKUTÍN, P. JÍŠA, D. KRUML, T. POLÁK, J.
Český název
Šíření krátkých únavových trhlin v hliníkové slitině EN AW-6082/T6
Anglický název
Small fatigue crack growth in aluminium alloy EN AW-6082/T6
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
The kinetics of small fatigue crack growth at room temperature was measured by a direct observation of the shallow notch on a cylindrical specimen. The growth of the crack was measured within the range of half surface crack length from ~10 micrometers up to ~2 mm. A linear dependence between the crack growth rate and the crack length, observed in case of steels, was confirmed to be valid in the aluminium 6082/T6 alloy, too. The crack growth coefficient kg increases with plastic strain amplitude; this dependence is well described by a power law. The fatigue life prediction based on the crack growth measurements is compared with the Manson-Coffin law.
Český abstrakt
Sledána byla kinetika šíření krátkých únavových trhlin vznikajících v mělkém vrubu na válcových vzorcích vyrobených z hliníkové slitiny EN AW-6082/T6. Šíření trhlin bylo měřeno v rozmezí délek cca 10 micrometrů až 2 mm. Byla potvrzena lineární závislost rychlosti šíření trhliny a délky trhliny.
Anglický abstrakt
The kinetics of small fatigue crack growth at room temperature was measured by a direct observation of the shallow notch on a cylindrical specimen. The growth of the crack was measured within the range of half surface crack length from ~10 micrometers up to ~2 mm. A linear dependence between the crack growth rate and the crack length, observed in case of steels, was confirmed to be valid in the aluminium 6082/T6 alloy, too. The crack growth coefficient kg increases with plastic strain amplitude; this dependence is well described by a power law. The fatigue life prediction based on the crack growth measurements is compared with the Manson-Coffin law.
Klíčová slova česky
slitina hliníku, krátká únavová trhlina, rychlost šíření trhliny, nukleace trhliny
Klíčová slova anglicky
aluminium alloy, small fatigue crack, crack crowth rate, crack nucleation
Rok RIV
2010
Vydáno
01.08.2010
Nakladatel
Elsevier
Místo
London
ISSN
0142-1123
Časopis
INTERNATIONAL JOURNAL OF FATIGUE
Ročník
32
Číslo
12
Strany od–do
1913–1920
Počet stran
8
BIBTEX
@article{BUT49753,
author="Petr {Liškutín} and David {Jíša} and Tomáš {Kruml} and Jaroslav {Polák},
title="Small fatigue crack growth in aluminium alloy EN AW-6082/T6",
journal="INTERNATIONAL JOURNAL OF FATIGUE",
year="2010",
volume="32",
number="12",
month="August",
pages="1913--1920",
publisher="Elsevier",
address="London",
issn="0142-1123"
}