Syntéza a zpracování vanadičnanu inditého

Synthesis and processing of InVO4

článek v časopise - ostatní, Jost

en

Indium vanadates for severe applications as photocatalysts, anodes for Li rechargeable batteries or electrochromic devices were prepared via conventional and non-conventional preparation methods. The conventional high temperature solid state reaction was performed at 800 C for 25 hours and the non-conventional microwave-assisted synthesis was performed at 220 C for different reaction times under hydrothermal conditions. The as-prepared powders were characterized in terms of phase composition by X-Ray diffraction analysis (XRD) and infrared spectroscopy (IR) and of powder morphology by scanning electron microscopy (SEM) and BET method. Nanosized indium vanadate powders were successfully synthesized by non-conventional microwave-assisted hydrothermal method. The dense ceramic bodies suitable for electrical conductivity measurements with 96% t.d. were obtained by sintering of powders prepared by high-temperature solid state reaction at 1100 C for 4 h with admission of oleic acid as a binder additive

Vanadičnan inditý je vhodným kandidátem pro různé aplikace – fotokatalytické reakce štěpení vody, anody v Li bateriích či různých elektrochromických zařízeních. Keramický prášek byl připraven konveneční a nenkonveční cestou. Konvenční metodou byl zvolena vysokoteplotní reakce v tuhé fázi při 800 C po 25h. Nekonvenční metodou byla zvolena mikrovlnná syntéza za hydrotermálních podmínek – 220 C a 60 bar. Připravené prášky byly studovány z hlediska fázového složení pomocí rentgenové difrakce (XDR) a infračervené mikroskopie (IR), dále z hlediska morfolgoie prášků pomocí reastrovací elektronové mirkroskopie (SEM) a velikosti částic (BET metoda) . Nanočásticový vanadišnan idnotý byl úspšně připraven pomocí nekonvenční mirkolvnné sysntézy za hydrotermálních podmínek. Zpracováním připravených prášků byla připravena objemová keramika vhodná pro testování elektrických vlastností materiálu. Slinováním při 1100 C po dobu 4h dosahovala hustota připravených těles až 96% t.h.. Úspěšná příprava bezdefektní hurné keramiky byla podmíněna příměsí pojivových aditiv – kyseliny olejové.

Indium vanadates for severe applications as photocatalysts, anodes for Li rechargeable batteries or electrochromic devices were prepared via conventional and non-conventional preparation methods. The conventional high temperature solid state reaction was performed at 800 C for 25 hours and the non-conventional microwave-assisted synthesis was performed at 220 C for different reaction times under hydrothermal conditions. The as-prepared powders were characterized in terms of phase composition by X-Ray diffraction analysis (XRD) and infrared spectroscopy (IR) and of powder morphology by scanning electron microscopy (SEM) and BET method. Nanosized indium vanadate powders were successfully synthesized by non-conventional microwave-assisted hydrothermal method. The dense ceramic bodies suitable for electrical conductivity measurements with 96% t.d. were obtained by sintering of powders prepared by high-temperature solid state reaction at 1100 C for 4 h with admission of oleic acid as a binder additive

vanadičnan inditý, mikrovlnná syntéza za hydrotermálních podmínek

Indium vanadate; microwave-assisted hydrothermal synthesis