Special fracture mechanics specimens for multilayer plastic pipes testing
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
Pipes consisting of layers of different materials (multilayer pipes) are considered. The fracture toughness value of the main pipe is taken into account as a parameter relevant to fracture assessment connected with the resistance of pipe material against slow crack growth. With the aim of simplifying estimation of main pipe material fracture toughness, non-homogeneous test specimens cut directly from multi-layer pipes are suggested and numerically analysed. The values of the corresponding stress intensity factor KI and biaxiality factors B are calculated for the case of two and three layer test specimens. Based on the results obtained, the transferability of fracture toughness values measured on laboratory specimens to pipe systems is discussed. It is shown that in most cases of multilayer commercial pipes and routine fracture toughness measurements the values of the stress intensity factor calculated on the basis of homogeneous specimens can be used.
Český abstrakt
Práce se zabývá návrhem speciálního zkušebního tělesa pro měření lomově-mechanických parametrů vícevrstvých polymerních trubek. V práci jsou navrženy 2 typy těles vhodných pro testování 3 bodovým ohybem a tahem.
Anglický abstrakt
Pipes consisting of layers of different materials (multilayer pipes) are considered. The fracture toughness value of the main pipe is taken into account as a parameter relevant to fracture assessment connected with the resistance of pipe material against slow crack growth. With the aim of simplifying estimation of main pipe material fracture toughness, non-homogeneous test specimens cut directly from multi-layer pipes are suggested and numerically analysed. The values of the corresponding stress intensity factor KI and biaxiality factors B are calculated for the case of two and three layer test specimens. Based on the results obtained, the transferability of fracture toughness values measured on laboratory specimens to pipe systems is discussed. It is shown that in most cases of multilayer commercial pipes and routine fracture toughness measurements the values of the stress intensity factor calculated on the basis of homogeneous specimens can be used.
Klíčová slova anglicky
Multilayer plastic pipes, C-type specimen, K-calibration, Fracture toughness, Slow crack growth, Non-homogenous specimens
Rok RIV
2009
Vydáno
07.07.2009
Nakladatel
Elsevier
Místo
Amsterdam, Nizozemí
ISSN
0142-9418
Časopis
POLYMER TESTING
Ročník
28
Číslo
8
Strany od–do
785–792
Počet stran
7
BIBTEX
@article{BUT49307,
author="Pavel {Hutař} and Lucie {Malíková} and Zdeněk {Knésl} and Eva {Nezbedová} and Luboš {Náhlík},
title="Special fracture mechanics specimens for multilayer plastic pipes testing",
journal="POLYMER TESTING",
year="2009",
volume="28",
number="8",
month="July",
pages="785--792",
publisher="Elsevier",
address="Amsterdam, Nizozemí",
issn="0142-9418"
}