Kontinuální lití sochorů a elektromagnetické míchání taveniny
STRÁNSKÝ, K. KAVIČKA, F. SEKANINA, B. ŠTĚTINA, J. STRÁNSKÝ, L.
Český název
Kontinuální lití sochorů a elektromagnetické míchání taveniny
Anglický název
A concast billet caster and electromagnetic stirring of the melt
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
Electromagnetic stirring (EMS) suppresses the growth of columnar crystals of billets and reduces the tendency to cracking during casting and at low temperatures. A caster was used for the testing of two induction stirrers – one on the actual mould and the other beneath the mould – to determine the effect of EMS on the formation of the structure of non-alloy steel. Experimental research was also confronted with results acquired from the application of the models of the temperature field and chemical heterogeneity and the physical-similarity theory. Statistical monitoring of the quality of concast billets has proven that stirring significantly reduces the occurrence of defects – in this case cracks.
Český abstrakt
Elektromagnetické míchání potlačuje růst sloupcových krystalů v sochorech a snižuje tendenci k tvorbě trhlin během lití a za nízkých teplot. Licí stroj byl použit pro testování dvou indukčních míchačů – na krystalizátoru a pod krystalizátorem – s cílem stanovit vliv elektromagnetického míchání na strukturu nelegované oceli. Experimentální výzkum byl porovnán s výsledky aplikace modelů teplotního pole a chemické heterogenity a teorií fyzikální podobnosti. Statistické monitorování kvality kontinuálně odlévaných sochorů ukazuje, že míchání významně snižuje přítomnost defektů – v tomto případě trhlin.
Anglický abstrakt
Electromagnetic stirring (EMS) suppresses the growth of columnar crystals of billets and reduces the tendency to cracking during casting and at low temperatures. A caster was used for the testing of two induction stirrers – one on the actual mould and the other beneath the mould – to determine the effect of EMS on the formation of the structure of non-alloy steel. Experimental research was also confronted with results acquired from the application of the models of the temperature field and chemical heterogeneity and the physical-similarity theory. Statistical monitoring of the quality of concast billets has proven that stirring significantly reduces the occurrence of defects – in this case cracks.
Klíčová slova česky
kontinuální lití, sochory, elektromagnetické míchání, defekty
Klíčová slova anglicky
concasting, billets, electromagnetic stirring, defects
Rok RIV
2009
Vydáno
20.10.2009
Nakladatel
IMŽ
Místo
Glivice
ISSN
0137-9941
Časopis
Prace Instytutu Metalurgii Zelaza
Ročník
61
Číslo
5
Strany od–do
142–145
Počet stran
4
BIBTEX
@article{BUT48709,
author="Karel {Stránský} and František {Kavička} and Bohumil {Sekanina} and Josef {Štětina} and Lubomír {Stránský},
title="A concast billet caster and electromagnetic stirring of the melt",
journal="Prace Instytutu Metalurgii Zelaza",
year="2009",
volume="61",
number="5",
month="October",
pages="142--145",
publisher="IMŽ",
address="Glivice",
issn="0137-9941"
}