Originální abstrakt

Cyclic plastic response of the Eurofer reduced activation ferritic-martensitic steel at room temperature was studied. Strain amplitude was kept constant during cycling. The softening curves in two representation were obtained. The fatigue life curve in NF = f(ea) representation and the cyclic stress-strain curve were determined. The main part of the study was focused on surface relief observation: determination of crack nucleation sites and kinetics of crack growth. The crack growth coefficient kg was measured, allowing the fatigue life predictions based on the kinetics of short crack growth. The fracture surfaces were observed using scanning electron microscopy (SEM). Nucleation sites, striation and other typical fatigue features were detected.

Český abstrakt

Byla studována cyklická odezva feriticko-martenzitické oceli Eurofer, zkoušky byly prováděny v řízení konstantní celkové deformace. Byly získány křivky únavového zpevnění a změkčení ve dvou reprezentacích. Byly získány křivky únavového života. Hlavní cíl práce byl zaměřen na pozorování iniciace krátkých trhlin a jejich následném růstu. Byly pozorovány lomové plochy a nalezeny typické prvky únavového poškození.

Anglický abstrakt

Cyclic plastic response of the Eurofer reduced activation ferritic-martensitic steel at room temperature was studied. Strain amplitude was kept constant during cycling. The softening curves in two representation were obtained. The fatigue life curve in NF = f(ea) representation and the cyclic stress-strain curve were determined. The main part of the study was focused on surface relief observation: determination of crack nucleation sites and kinetics of crack growth. The crack growth coefficient kg was measured, allowing the fatigue life predictions based on the kinetics of short crack growth. The fracture surfaces were observed using scanning electron microscopy (SEM). Nucleation sites, striation and other typical fatigue features were detected.

Klíčová slova česky

nízkocyklová únava, šíření krátkých trhlin, únavové změkčení

Klíčová slova anglicky

low cycle fatigue, short crack propagation, fatigue softening

Rok RIV

2009

Vydáno

10.07.2009

Místo

Žilina, Slovensko

ISSN

1335-0803

Časopis

Materiálové inžinierstvo

Ročník

XVI

Číslo

3a/2009

Strany od–do

32–36

Počet stran

5

BIBTEX


@article{BUT48616,
  author="Ivo {Kuběna} and Tomáš {Kruml},
  title="FATIGUE PROPERTIES AND CRACK GROWTH IN EUROFER STEEL",
  journal="Materiálové inžinierstvo",
  year="2009",
  volume="XVI",
  number="3a/2009",
  month="July",
  pages="32--36",
  address="Žilina, Slovensko",
  issn="1335-0803"
}