Detail publikace
Chemické složení a morfologie oxidické keramiky při filtrování oceli dezoxidované hliníkem
BAŽAN, J. STRÁNSKÝ, K. HORÁKOVÁ, D.
Český název
Chemické složení a morfologie oxidické keramiky při filtrování oceli dezoxidované hliníkem
Anglický název
Chemical Composition and Morphology of Oxidic Ceramics at Filtration of Steel Deoxidised by Aluminium
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
Composition and morphology of filter ceramics was investigated during filtration of steel deoxidized by aluminium. Filtration was realized with use of filters based on oxidic ceramics Cr2O3, TiO2, SiO2, ZrO2, Al2O3, 3Al2Os.2SiO2 and MgO.Al2O3. It was established that change of interphase (coating) occurs during filtration of steel on the surface of capillaries of ceramics, where content of basic oxidic component decreases. Loss of oxidic component in the coating is replaced by increase of oxides of manganese and iron and it is great extent inversely proportional to the value of Gibbs energy of oxide, which forms this initial basis of ceramics.
Český abstrakt
Bylo studováno chemické složení a morfologie keramických filtrů během filtrování oceli, která byla dezoxidována hliníkem. Byly použity filtry na bázi oxidické keramiky Cr2O3, TiO2, SiO2, ZrO2, Al2O3, 3Al2Os.2SiO2 and MgO.Al2O3. Bylo zjištěno, že na rozhraní (povlaku) na povrchu filtru během filtrace oceli se snižuje množství oxidických fází. Ztráta oxidických složek na povrchu (povlaku) je nahrazena oxidy manganu a železa.
Anglický abstrakt
Composition and morphology of filter ceramics was investigated during filtration of steel deoxidized by aluminium. Filtration was realized with use of filters based on oxidic ceramics Cr2O3, TiO2, SiO2, ZrO2, Al2O3, 3Al2Os.2SiO2 and MgO.Al2O3. It was established that change of interphase (coating) occurs during filtration of steel on the surface of capillaries of ceramics, where content of basic oxidic component decreases. Loss of oxidic component in the coating is replaced by increase of oxides of manganese and iron and it is great extent inversely proportional to the value of Gibbs energy of oxide, which forms this initial basis of ceramics.
Klíčová slova česky
Filtrace oceli, keramické filtry, mezifázové reakce, termodynamická stabilita filtru
Klíčová slova anglicky
Filtration of steel, ceramic filters, interphase reactions, thermodynamic stability of filter
Rok RIV
2009
Vydáno
01.11.2009
Nakladatel
HMD, CMS Croatia
Místo
Zagreb, Croatia
ISSN
0543-5846
Časopis
Metalurgija
Ročník
48
Číslo
4
Strany od–do
229–234
Počet stran
6
BIBTEX
@article{BUT48193,
author="Jiří {Bažan} and Karel {Stránský} and Dana {Horáková},
title="Chemical Composition and Morphology of Oxidic Ceramics at Filtration of Steel Deoxidised by Aluminium",
journal="Metalurgija",
year="2009",
volume="48",
number="4",
month="November",
pages="229--234",
publisher="HMD, CMS Croatia",
address="Zagreb, Croatia",
issn="0543-5846"
}