Detail publikace
Příčné šíření trhlin ve vrstevnatých materiálech: stanovení rychlosti šíření únavové trhliny
NÁHLÍK, L. HUTAŘ, P. KNÉSL, Z.
Český název
Příčné šíření trhlin ve vrstevnatých materiálech: stanovení rychlosti šíření únavové trhliny
Anglický název
Transverse cracking of layered structures: evaluation of fatigue crack propagation
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
The objective of this paper is to investigate the transverse fatigue cracking of layered structures. To this end a fatigue crack propagation rate for a crack growing perpendicularly through the interfaces between individual layers of the structure is estimated. The suggested procedure takes into account the influence of different material properties of the layers on the stress field around the fatigue crack and the change of the stress singularity exponent in the special case of a crack touching the material interface. The assumptions of linear elastic fracture mechanics and elastic behaviour of the composite are considered. It is shown that the existence of the interfaces can have a negative influence on the residual fatigue life of layered structures.
Český abstrakt
Cílem práce je studium příčného praskání vrstevnatých materiálů. Je navržena procedura umožňující odhadnout rychlost šíření únavové trhliny v okolí rozhraní jednotlivých vrstev kompozitu, jenž bere v úvahu změnu singularity napětí v místě rozhraní.
Anglický abstrakt
The objective of this paper is to investigate the transverse fatigue cracking of layered structures. To this end a fatigue crack propagation rate for a crack growing perpendicularly through the interfaces between individual layers of the structure is estimated. The suggested procedure takes into account the influence of different material properties of the layers on the stress field around the fatigue crack and the change of the stress singularity exponent in the special case of a crack touching the material interface. The assumptions of linear elastic fracture mechanics and elastic behaviour of the composite are considered. It is shown that the existence of the interfaces can have a negative influence on the residual fatigue life of layered structures.
Klíčová slova česky
vrstevnaté kompozity, bi-materiálové rozhraní, efektivní součinitel intenzity napětí
Klíčová slova anglicky
layered composites, bi-material interface, effective stress intensity factor.
Rok RIV
2008
Vydáno
01.01.2008
Nakladatel
Trans Tech Publications
Místo
Switzerland
ISSN
0255-5476
Časopis
Materials Science Forum
Ročník
567-568
Číslo
xxx
Strany od–do
221–224
Počet stran
4
BIBTEX
@article{BUT46791,
author="Luboš {Náhlík} and Pavel {Hutař} and Zdeněk {Knésl},
title="Transverse cracking of layered structures: evaluation of fatigue crack propagation",
journal="Materials Science Forum",
year="2008",
volume="567-568",
number="xxx",
month="January",
pages="221--224",
publisher="Trans Tech Publications",
address="Switzerland",
issn="0255-5476"
}