Český název
Vliv tlaku na interakci mezi korund-mulitovou formou a roztavenými niklovými slitinami
Anglický název
Influence of Pressure on the Interaction between Alumina-Mullite Shell Moulds and Molten Nickel Alloys
Typ
článek v časopise - ostatní, Jost
Jazyk
en
Originální abstrakt
The interaction of ceramic alumina-mullite mould with nickel and nickel alloys (ZhS6K, NiTi and NiCr) was studied at a temperature of 1773K in the pressure range from 0.1 Pa to 1 atm. The ceramic mould contained a continuous network of pores, which provided for the releasing of the gaseous phase at the mould/metal interface and thus facilitated physical and chemical erosion of the face layer of the mould at low pressures. Increasing the pressure of gaseous atmosphere to over 0.1 atm practically prevented the erosion of mould surface by nickel and its alloys.
Český abstrakt
Byla studována interakce keramických korund-mulitových forem s niklem a jeho slitinami (ŽS6K, NiCr a NiTi) za teploty 1500C a tlacích od 0,1 Pa do 1 atm. Keramické formy obsahovaly spojitou síť pórů, což umožnilo přístup plynné fáze na rozhraní roztavený kov/forma a napomohlo fyzikální a chemické erozi lícní vrstvy formy při nízkých tlacích. Zvýšení tlaku okolní inertní atmosféry nad 0,1 atm prakticky zabránilo erozi formy kovem.
Anglický abstrakt
The interaction of ceramic alumina-mullite mould with nickel and nickel alloys (ZhS6K, NiTi and NiCr) was studied at a temperature of 1773K in the pressure range from 0.1 Pa to 1 atm. The ceramic mould contained a continuous network of pores, which provided for the releasing of the gaseous phase at the mould/metal interface and thus facilitated physical and chemical erosion of the face layer of the mould at low pressures. Increasing the pressure of gaseous atmosphere to over 0.1 atm practically prevented the erosion of mould surface by nickel and its alloys.
Klíčová slova anglicky
ceramic, metal, interaction
Vydáno
01.01.1995
Nakladatel
Institute of Chemical Technology in Prague and Academy of Sciences of the Czech Republic
ISSN
0862-5468
Časopis
Ceramics-Silikáty
Ročník
39
Číslo
4
Strany od–do
145–154
Počet stran
10
BIBTEX
@article{BUT46660,
author="Jaroslav {Cihlář} and Karel {Maca} and Peter {Marquis},
title="Influence of Pressure on the Interaction between Alumina-Mullite Shell Moulds and Molten Nickel Alloys",
journal="Ceramics-Silikáty",
year="1995",
volume="39",
number="4",
month="January",
pages="145--154",
publisher="Institute of Chemical Technology in Prague and Academy of Sciences of the Czech Republic",
issn="0862-5468"
}