Mikrostrukturní analýza únavových prahových hodnot v duplexní nerezové oceli
POKLUDA, J. PODRÁBSKÝ, T. SLÁMEČKA, K. POSPÍŠILOVÁ, S. CHAI, G.
Český název
Mikrostrukturní analýza únavových prahových hodnot v duplexní nerezové oceli
Anglický název
Microstructure-aided Analysis of Fatigue Thresholds in Duplex Stainless Steel
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
High fatigue threshold values of duplex ferritic-martensitic steels are interpreted by using a unified model of roughness- and plasticity induced crack closure. Complex metallographical and fractographical analysis was performed in order to obtain characteristics of tortuous crack paths produced by crack deflection and branching mainly at austenite/ferrite interfaces. Calculated values of effective thresholds are in a good agreement with experimental data. The total level of extrinsic toughening (closure + shielding) induced by the duplex microstructure was determined to be as much as 70% of measured fatigue threshold values. This is the main reason for the high resistance to propagation of long fatigue cracks in the near-threshold region.
Český abstrakt
Únavové prahové hodnoty duplexní feriticko-martensitické oceli jsou interpretovány užitím zobecněného modelu drsnostně a plasticky indukovaného zavírání trhliny. Komplexní metalografická a fraktografická analýza byla užita k získání charakteristik křivolaké trhliny přednostně na rozhraní austenit/ferit. Spočtené hodnoty efektivních prahových hodnot jsou v dobré shodě s experimentálními daty. Celková úroveň extrinsitního zhouževnatění indukovaného duplexní mikrostrukturou byla určena jako 70% měřených prahových hodnot.
Anglický abstrakt
High fatigue threshold values of duplex ferritic-martensitic steels are interpreted by using a unified model of roughness- and plasticity induced crack closure. Complex metallographical and fractographical analysis was performed in order to obtain characteristics of tortuous crack paths produced by crack deflection and branching mainly at austenite/ferrite interfaces. Calculated values of effective thresholds are in a good agreement with experimental data. The total level of extrinsic toughening (closure + shielding) induced by the duplex microstructure was determined to be as much as 70% of measured fatigue threshold values. This is the main reason for the high resistance to propagation of long fatigue cracks in the near-threshold region.
Klíčová slova česky
Prahové únavové hodnoty, duplexní ocel, vyhnutí trhliny, větvení trhliny, extrinsitní zhouževnatění, zobecněný model zavírání trhliny
Klíčová slova anglicky
Fatigue thresholds, duplex steel, crack deflection, crack branching, extrinsic toughening, unified closure model
Rok RIV
2008
Vydáno
23.01.2008
ISSN
0255-5476
Časopis
Materials Science Forum
Ročník
567-568
Číslo
1
Strany od–do
101–104
Počet stran
4
BIBTEX
@article{BUT45344,
author="Jaroslav {Pokluda} and Tomáš {Podrábský} and Karel {Slámečka} and Simona {Hutařová} and Guocai {Chai},
title="Microstructure-aided Analysis of Fatigue Thresholds in Duplex Stainless Steel",
journal="Materials Science Forum",
year="2008",
volume="567-568",
number="1",
month="January",
pages="101--104",
issn="0255-5476"
}