Originální abstrakt
Damage of multi-layer commercial plastic pipes with dimensional integrated protective surfaces was investigated. Fracture toughness was chosen as a parameter relevant to evaluation of the resistance of pipe material to slow crack growth. A special type of a C-shaped non-homogeneous fracture mechanics specimen machined directly from the pipe was suggested, numerically analyzed and tested. To describe the influence of the interface between different material layers of the C-shaped specimen on crack behavior, a modification of standard crack fracture mechanics was used. Transferability of the fracture mechanics parameters obtained from a small laboratory C-type specimen to pipe systems was discussed using a constraint-based two-parameter fracture mechanics approach.
Český abstrakt
Bylo studováno poškození vícevrstvých komerčních plastických trubek s ochrannými povrchy. Jako příslušný parametr pro vyčíslení odolnosti materiálu trubky proti pomalému šíření trhliny byla vybrána lomová houževnatost. Bylo navrženo speciální nehomogenní zkušební těleso tvaru C, které bylo následně numericky analyzováno a testováno. Pro popis vlivu rozhraní mezi jednotlivými materiálovými vrstvami C-tělesa na chování trhliny byla využita modifikace klasického lineárně elastické lomové mechaniky. S využitím přístupu dvouparametrové lomové mechaniky založeného na "constraint" efektu byla diskutována přenositelnost parametrů zjištěných na malém laboratorním C-tělese na reálný potrubní systém.
Anglický abstrakt
Damage of multi-layer commercial plastic pipes with dimensional integrated protective surfaces was investigated. Fracture toughness was chosen as a parameter relevant to evaluation of the resistance of pipe material to slow crack growth. A special type of a C-shaped non-homogeneous fracture mechanics specimen machined directly from the pipe was suggested, numerically analyzed and tested. To describe the influence of the interface between different material layers of the C-shaped specimen on crack behavior, a modification of standard crack fracture mechanics was used. Transferability of the fracture mechanics parameters obtained from a small laboratory C-type specimen to pipe systems was discussed using a constraint-based two-parameter fracture mechanics approach.
Klíčová slova česky
polyetylen, vícevrstvé trubky, lomová houževnatost, stísnění
Klíčová slova anglicky
polyethylene, multi-layer pipes, fracture toughness, constraint
Rok RIV
2007
Vydáno
09.12.2007
Nakladatel
CSIR
Místo
Port Elizabeth, South Africa
ISBN
978-0-620-37679-2
Kniha
Fibre Reinforced Composites Conference 2007
Strany od–do
61–73
Počet stran
13
BIBTEX
@inproceedings{BUT27925,
author="Eva {Nezbedová} and Zdeněk {Knésl} and Lucie {Malíková} and Bohumil {Vlach},
title="Fracture Mechanics Analysis of Multi-Layer Pipes",
booktitle="Fibre Reinforced Composites Conference 2007",
year="2007",
month="December",
pages="61--73",
publisher="CSIR",
address="Port Elizabeth, South Africa",
isbn="978-0-620-37679-2"
}