Ultrajemný nikl a jeho nanokompozit připravený elektrolytickým pokovováním

CIHLÁŘOVÁ, P. ŠVEJCAR, J.

Český název

Ultrajemný nikl a jeho nanokompozit připravený elektrolytickým pokovováním

Anglický název

ELECTRODEPOSITED NICKEL AND ITS PARTICLE-REINFORCED NANOCOMPOSITE

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

There are two types of experimental materials used pure nickel and its nanocomposite reinforced by nano-sized SiO2. These materials were produced by TU Clausthal, Germany. The material was deposited on copper substrate by electrodeposition under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain free-standing samples for the creep testing. The creep tests were carried out at temperatures from 293 to 573 K and the applied stress ranged from 125 to 700 MPa. Fracture details were observed by scanning electron microscope PHILIPS XL 30

Český abstrakt

Nanostrukturní čistý nikl a jeho nanokompozit byly připraveny elektrolytickým pokovováním na měděném substrátu za těchto podmínek:stejnosměrný proud 25mA, 30hod. Měděná podložka byla mechanicky odstraněna a tím byl získán experimentální materiál pro mechanické a creepové zkoušky. Předmětem studia bylo srovnání tahových a creepových vlastností elektrolyticky nanášeného čistého niklu a jeho kompozitu s nanometrickými částicemi SiO2. Creepové zkoušky byly provedeny v rozsahu teplot od 293K do 473K. Experimentální materiál (Ni a Ni+SiO2) byl studován pomocí REM a TEM. Studium bylo především zaměřeno na rozložení částic SiO2 v matrici a velikost zrn matrice i částic.

Anglický abstrakt

There are two types of experimental materials used pure nickel and its nanocomposite reinforced by nano-sized SiO2. These materials were produced by TU Clausthal, Germany. The material was deposited on copper substrate by electrodeposition under these conditions: direct current, 25 mA and 30 h. After electroplating, the copper substrate was metallographically ground out to obtain free-standing samples for the creep testing. The creep tests were carried out at temperatures from 293 to 573 K and the applied stress ranged from 125 to 700 MPa. Fracture details were observed by scanning electron microscope PHILIPS XL 30

Klíčová slova anglicky

nickel, nanocomposite, creep

Rok RIV

2006

Vydáno

27.06.2006

Nakladatel

Royal Microscopical Society, Oxford, UK

Místo

Royal Microscopical Society, Oxford, UK

Kniha

Microscience 2006

Číslo edice

1

Počet stran

1

BIBTEX


@inproceedings{BUT25108,
  author="Petra {Cihlářová} and Jiří {Švejcar},
  title="ELECTRODEPOSITED NICKEL AND ITS PARTICLE-REINFORCED NANOCOMPOSITE",
  booktitle="Microscience 2006",
  year="2006",
  month="June",
  publisher="Royal Microscopical Society, Oxford, UK",
  address="Royal Microscopical Society, Oxford, UK"
}