Originální abstrakt
High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain. Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation.
Český abstrakt
Práca predstavuje experimentálne výsledky charakterizujúce interakciu vysokocyklovej únavy a creepu u liatej Ni-superzliatine IN713LC. Príspevok vysvetľuje vplyv ťahového stredného napatia a superponácie amplitúdy napatia na stredné napatie na životnosť a sposob porušenia daného materiálu.
Anglický abstrakt
High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain. Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation.
Klíčová slova anglicky
IN713LC, creep-fatigue interaction, mean stress
Rok RIV
2006
Vydáno
30.11.2006
Nakladatel
AVČR, Brno
Místo
Brno
ISBN
80-239-8271-0
Kniha
Víceúrovňový design pokrokových materiálů
Strany od–do
119–127
Počet stran
8
BIBTEX
@inproceedings{BUT21726,
author="Rastislav {Mintách},
title="High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress",
booktitle="Víceúrovňový design pokrokových materiálů",
year="2006",
month="November",
pages="119--127",
publisher="AVČR, Brno",
address="Brno",
isbn="80-239-8271-0"
}