Originální abstrakt
The resistance of coated structures to fatigue failure of substrate is investigated. In order to quantify the influence of elastic mismatch of coating and substrate on the fatigue threshold applied stress, a simplified approach based on calculations of crack mouth opening displacement CMOD has been suggested. It is concluded that the resistance of the substrate to fatigue damage significantly decreases for cases of hard coatings on a stiffer substrate. Traditional approaches may have underestimated the effect and estimations of the residual fatigue life of coated structures neglecting this fact could lead to non-conservative values and thus cause unexpected failures.
Český abstrakt
V práci je vyšetřován odpor povlakovaných součástí vzhledem k únavovému porušení podkladu. Je zde navržen zjednodušený přístup, který je založen na otevření trhliny na povrchu součásti, umožňující kvantifikovar vliv elastického mismatch povlakovaných součástí na prahovou únavovou hodnotu napětí. Je ukázáno, že odpor podkladu vůči únavovému poškození výrazně klesá pro tvrdý povlak na poddajnějším podkladu. Tradiční přístupy mohou podhodnotit tento vliv a zanedbání této skutečnosti při hodnocení zbytkové životnosti povlakovaných součástí může vést k nekonzervativním hodnotám a způsobit tak neočekávné havárie.
Anglický abstrakt
The resistance of coated structures to fatigue failure of substrate is investigated. In order to quantify the influence of elastic mismatch of coating and substrate on the fatigue threshold applied stress, a simplified approach based on calculations of crack mouth opening displacement CMOD has been suggested. It is concluded that the resistance of the substrate to fatigue damage significantly decreases for cases of hard coatings on a stiffer substrate. Traditional approaches may have underestimated the effect and estimations of the residual fatigue life of coated structures neglecting this fact could lead to non-conservative values and thus cause unexpected failures.
Klíčová slova anglicky
crack mouth opening displacement, crack propagtion, bimaterial interface
Rok RIV
2005
Vydáno
01.08.2005
Místo
Tenerife, Canary Islands
Kniha
ICCE-12 Twelth Annual International Conference on Composites/Nano Engineering
Strany od–do
153–154
Počet stran
2
BIBTEX
@inproceedings{BUT21716,
author="Zdeněk {Knésl} and Pavel {Bareš} and Luboš {Náhlík},
title="EVALUATION OF THE FATIGUE THRESHOLD OF COATED STRUCTURES",
booktitle="ICCE-12 Twelth Annual International Conference on Composites/Nano Engineering",
year="2005",
month="August",
pages="153--154",
address="Tenerife, Canary Islands"
}