Microstructural stability and precipitate evolution of thermally treated 7075 aluminum alloy fabricated by cold spray

článek v časopise ve Web of Science, Jimp

en

In this work, the effects of post-deposition heat treatment on microstructural stability of cold sprayed AA7075 aluminum coatings were thoroughly characterized. The as-atomized powder and annealed coatings were investigated using scanning electron microscopy, electron back-scattered diffraction, and microhardness measurements. Scanning transmission electron microscopy was further employed to evaluate grain/subgrain structure near the particle interface region. Precipitation in the coating was studied through differential scanning calorimetry and X-ray diffraction. The feedstock powder revealed dendritic/cellular-like structure accompanied by microsegregations of the main alloying elements at dendrite boundaries. The high-pressure Cold Spray process led to formation of lamellar subgrains and UFG grains via dynamic recovery/recrystallization mechanisms. GP zones present in the AA7075 powder continuously reprecipitated into more stable η´/η phases owing to propellant gas heating and extensive plastic strains induced during cold spraying. The applied annealing resulted in progressive softening of the AA7075 coatings and gradual transformation of LAGBs into HAGBs. The solute-rich grain boundary network observed in powder microstructure was fully retained after CS deposition but decomposed into coarse η and S precipitates upon high-temperature annealing. The CS AA7075 coating showed decent thermal stability up to 300 °C and rapid grain growth at 400 °C. The relationship between precipitate size and thermal stability was further discussed in terms of the Zener pinning theory.

In this work, the effects of post-deposition heat treatment on microstructural stability of cold sprayed AA7075 aluminum coatings were thoroughly characterized. The as-atomized powder and annealed coatings were investigated using scanning electron microscopy, electron back-scattered diffraction, and microhardness measurements. Scanning transmission electron microscopy was further employed to evaluate grain/subgrain structure near the particle interface region. Precipitation in the coating was studied through differential scanning calorimetry and X-ray diffraction. The feedstock powder revealed dendritic/cellular-like structure accompanied by microsegregations of the main alloying elements at dendrite boundaries. The high-pressure Cold Spray process led to formation of lamellar subgrains and UFG grains via dynamic recovery/recrystallization mechanisms. GP zones present in the AA7075 powder continuously reprecipitated into more stable η´/η phases owing to propellant gas heating and extensive plastic strains induced during cold spraying. The applied annealing resulted in progressive softening of the AA7075 coatings and gradual transformation of LAGBs into HAGBs. The solute-rich grain boundary network observed in powder microstructure was fully retained after CS deposition but decomposed into coarse η and S precipitates upon high-temperature annealing. The CS AA7075 coating showed decent thermal stability up to 300 °C and rapid grain growth at 400 °C. The relationship between precipitate size and thermal stability was further discussed in terms of the Zener pinning theory.

Cold spray, aluminum alloy 7075, microstructure, DSC

01.08.2024

ELSEVIER

NEW YORK

1873-4189

216

114259

114259–114259

12