Direct comparison between Co-28Cr-6Mo alloy prepared by Selective Laser Melting and traditional investment casting

ROUDNICKÁ, M. BIGAS, J. ŠREIBR, V. PALOUŠEK, D. DALIBOR, V.

Anglický název

Direct comparison between Co-28Cr-6Mo alloy prepared by Selective Laser Melting and traditional investment casting

Typ

článek ve sborníku mimo WoS a Scopus

Jazyk

en

Originální abstrakt

Thanks to high mechanical properties stable at elevated temperatures, high abrasion resistance, suitable corrosion resistance and biocompatibility, ternary cobalt alloy Co-28Cr-6Mo is a widely used material in the field of aviation industry and medical implants production. Due to the difficult formability and machinability of this alloy in combination with complex shapes of produced parts, investment casting is the mostly employed production process. However, additive manufacturing provides new processing opportunities. E.g. Selective Laser Melting (SLM) technology fusing metallic powders by precisely focused and controlled laser beam enables the production of highly complex parts with high precision. In this contribution, we bring a direct comparison between the microstructures and mechanical properties of Co-28Cr-6Mo alloy prepared by SLM and investment casting. Due to significant differences in microstructure fineness and phase composition, SLM is revealed to increase not only material strength and hardness but concurrently plasticity. As a result of rapid solidification during SLM, very fine cellular microstructure with Mo microsegregation at cell walls is formed without the occurrence of any secondary phases. The distinctive microstructure of the additively manufactured alloy can be expected to be the cause of many other variances in the material behaviour.

Anglický abstrakt

Thanks to high mechanical properties stable at elevated temperatures, high abrasion resistance, suitable corrosion resistance and biocompatibility, ternary cobalt alloy Co-28Cr-6Mo is a widely used material in the field of aviation industry and medical implants production. Due to the difficult formability and machinability of this alloy in combination with complex shapes of produced parts, investment casting is the mostly employed production process. However, additive manufacturing provides new processing opportunities. E.g. Selective Laser Melting (SLM) technology fusing metallic powders by precisely focused and controlled laser beam enables the production of highly complex parts with high precision. In this contribution, we bring a direct comparison between the microstructures and mechanical properties of Co-28Cr-6Mo alloy prepared by SLM and investment casting. Due to significant differences in microstructure fineness and phase composition, SLM is revealed to increase not only material strength and hardness but concurrently plasticity. As a result of rapid solidification during SLM, very fine cellular microstructure with Mo microsegregation at cell walls is formed without the occurrence of any secondary phases. The distinctive microstructure of the additively manufactured alloy can be expected to be the cause of many other variances in the material behaviour.

Klíčová slova anglicky

Co-28Cr-6Mo; Additive manufacturing; Laser powder bed fusion; Elevated temperature operation

Vydáno

22.09.2021

Nakladatel

IOP Publishing

ISSN

1757-8981

Ročník

1178

Číslo

1

Strany od–do

1–6

Počet stran

6

BIBTEX


@inproceedings{BUT175127,
  author="Michaela {Roudnická} and Jiří {Bigas} and Vít {Šreibr} and David {Paloušek} and Vojtěch {Dalibor},
  title="Direct comparison between Co-28Cr-6Mo alloy prepared by Selective Laser Melting and traditional investment casting",
  year="2021",
  volume="1178",
  number="1",
  month="September",
  pages="1--6",
  publisher="IOP Publishing",
  issn="1757-8981"
}