ÚČINKY PRECIPITACE V-KARBIDŮ NA PEVNOST V TAHU A ÚNAVU TEPELNÝCH ZPRACOVANÝCH OCELÍ
OLINA, A. PÍŠKA, M.
Český název
ÚČINKY PRECIPITACE V-KARBIDŮ NA PEVNOST V TAHU A ÚNAVU TEPELNÝCH ZPRACOVANÝCH OCELÍ
Anglický název
THE EFFECT OF V-CARBIDES PRECIPITATION ON TENSILE AND FATIGUE PROPERTIES OF HEAT TREATED SPRING STEELS
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
en
Originální abstrakt
This paper deals with a comparison between the standard spring steel grade 0.54C-1.45Si-0.7Mn-0.7Cr and a grade micro-alloyed spring steel with 0.12 % V in terms of microstructure, grain refinement, strength and ductile properties. The micro-alloyed steel is supposed to provide a better performance as it had been proven for hot-rolled and heat treated wire. The vanadium micro-alloyed steel grades are quenched in oil typically, so high strengths and high ductility can be expected. It has been confirmed especially for induction heat treatment and quenching temperatures 810-910 °C, and the tempering temperatures 430 °C and 450 °C. That phenomenon can be explained with the strengthening effect and precipitation of vanadium carbides that suppress the grain coarsening effectively. The mechanism has been confirmed with electron scanning and transmission microscopy.
Český abstrakt
Tato práce se zabývá srovnáním vlastnostní standardní oceli pro pružiny o hmotnostním složení 0,54C – 1,45Si – 0,7Mn – 0,7Cr a mikrolegované oceli pro pružiny z oceli s 0,12% V z hlediska mikrostruktury, zjemnění zrna, pevnosti a tvařitelných vlastností. Mikrolegovaná ocel by měla poskytovat lepší výkon, jak bylo prokázáno u drátu válcovaného za tepla a tepelného zpracování. Typy vanadia z mikrolegované oceli jsou typicky kaleny do oleje, takže lze očekávat vysokou pevnost a vysokou tažnost. Bylo potvrzeno zejména při indukčním tepelném zpracování a teplotách při kalení 810-910 ° C a při temperoračních teplotách 430 ° C a 450 ° C. Tento jev lze vysvětlit precipitací karbidů vanadu, které účinně potlačují růst zrna. Mechanismus byl potvrzen pomocí elektronové skenovací a transmisní mikroskopie.
Anglický abstrakt
This paper deals with a comparison between the standard spring steel grade 0.54C-1.45Si-0.7Mn-0.7Cr and a grade micro-alloyed spring steel with 0.12 % V in terms of microstructure, grain refinement, strength and ductile properties. The micro-alloyed steel is supposed to provide a better performance as it had been proven for hot-rolled and heat treated wire. The vanadium micro-alloyed steel grades are quenched in oil typically, so high strengths and high ductility can be expected. It has been confirmed especially for induction heat treatment and quenching temperatures 810-910 °C, and the tempering temperatures 430 °C and 450 °C. That phenomenon can be explained with the strengthening effect and precipitation of vanadium carbides that suppress the grain coarsening effectively. The mechanism has been confirmed with electron scanning and transmission microscopy.
Klíčová slova česky
pružinová ocel, mikro-legování, karbidy vanadu, precipitáty, plasticita
Klíčová slova anglicky
spring steel, micro-alloying, vanadium carbides, precipitates, plasticity
Vydáno
15.04.2018
Nakladatel
Tanger Ltd.
Místo
Ostrava
ISBN
978-80-87294-79-6
Kniha
METAL 2017
Číslo edice
1
Strany od–do
949–955
Počet stran
6
BIBTEX
@inproceedings{BUT147167,
author="Anna {Olina} and Miroslav {Píška},
title="THE EFFECT OF V-CARBIDES PRECIPITATION ON TENSILE AND FATIGUE PROPERTIES OF HEAT TREATED SPRING STEELS",
booktitle="METAL 2017",
year="2018",
month="April",
pages="949--955",
publisher="Tanger Ltd.",
address="Ostrava",
isbn="978-80-87294-79-6"
}