Detail publikace

KVALITA POVRCHU HLINÍKOVÉ SLITINY PO WEDM

MOURALOVÁ, K. KOVÁŘ, J. KLAKURKOVÁ, L. KALIVODA, M.

Český název

KVALITA POVRCHU HLINÍKOVÉ SLITINY PO WEDM

Anglický název

Quality of aluminium alloy surface after WEDM

Typ

článek v časopise ve Scopus, Jsc

Jazyk

en

Originální abstrakt

Efficient machining using wire electrical discharge machining (WEDM) technology is a compromise between cutting speed and resulting surface quality. Typical morphology of the surface machined by WEDM shows a plenty of craters caused by electrospark discharges produced during the cutting process. This work is focused on assessing the impact of machine setting parameters on quantitative and qualitative evaluation of the workpiece surface of aluminium alloy AlZn6Mg2Cu. Using metallography, the surface effects arisen during the process of wire spark erosion on cross-sections of preparations were studied. Using local spot EDX microanalysis, the chemical composition of the surfaces of the samples was studied. The attention was also paid to the highest height of profile of the craters, which were studied using 3D filtered images.

Český abstrakt

Efektivní obrábění pomocí technologie elektroerozivního drátového řezání (WEDM) je kompromisem mezi rychlostí řezání a výslednou kvalitou povrchu. Typická morfologie elektroerozivně obrobeného povrchu se vyznačuje velkým množstvím kráterů způsobených elektrojiskrovými výboji vznikajících v průběhu řezného procesu. Práce je zaměřena na hodnocení vlivu parametrů nastavení stroje na kvantitativní I kvalitativní vyhodnocení povrchu obrobku z hliníkové slitiny AlZn6Mg2Cu. S využitím metalografie byly studovány povrchové jevy vzniklé v průběhu procesu elektroeroze na příčných řezech preparátů. Pomocí lokální bodové EDX mikroanalýzy bylo studováno chemické složení na površích vzorků. Pozornost byla věnována i nejvyšší výšce profilu kráterů, která byla studována pomocí 3D filtrovaných snímků.

Anglický abstrakt

Efficient machining using wire electrical discharge machining (WEDM) technology is a compromise between cutting speed and resulting surface quality. Typical morphology of the surface machined by WEDM shows a plenty of craters caused by electrospark discharges produced during the cutting process. This work is focused on assessing the impact of machine setting parameters on quantitative and qualitative evaluation of the workpiece surface of aluminium alloy AlZn6Mg2Cu. Using metallography, the surface effects arisen during the process of wire spark erosion on cross-sections of preparations were studied. Using local spot EDX microanalysis, the chemical composition of the surfaces of the samples was studied. The attention was also paid to the highest height of profile of the craters, which were studied using 3D filtered images.

Klíčová slova česky

WEDM, elektroerozivní obrábění, ovlivněná vrstva, hliníková slitina, kvalita povrchu

Klíčová slova anglicky

WEDM, electrical discharge machining, impact layer, aluminium alloy, quality of surface

Vydáno

10.02.2017

Nakladatel

MM Science Journal

Místo

Praha

ISSN

1803-1269

Ročník

2017

Číslo

1

Strany od–do

1679–1682

Počet stran

4

BIBTEX


@article{BUT132974,
  author="Kateřina {Mouralová} and Jiří {Kovář} and Lenka {Klakurková} and Milan {Kalivoda},
  title="Quality of aluminium alloy surface after WEDM",
  year="2017",
  volume="2017",
  number="1",
  month="February",
  pages="1679--1682",
  publisher="MM Science Journal",
  address="Praha",
  issn="1803-1269"
}