SCHOTTKYHO SOLÁRNÍ ČLÁNEK S ROZHRANÍM GRAFEN/AL2O3/SI

SCHOTTKY SOLAR CELL WITH GRAPHENE/AL2O3/SI INTERFACE

článek ve sborníku ve WoS nebo Scopus

en

In the field of applied research the combination of graphene and a semiconductor to form a Schottky solar cell (SSC) was found to be very significant. When compared to other types of solar cells being developed (organic or perovskite solar cells), the simple production process is an undisputable advantage of an SSC composed of graphene and silicon semiconductor. This simplicity and compatibility with well-established semiconductor technologies ultimately result in a low production price. The main problem relating to the Schottky solar cells with a graphene/silicon interface is the decreased efficiency of photocharge collection due to a recombination on the interface. In order to decrease the effect on the efficiency due to the recombination, the graphene/silicon interface has been modified with 2 nm Al2O3.

V oblasti aplikovaného výzkumu solárních článků byla shledána kombinace grafenu a polovodiče za účelem vytvoření Schottkyho solárního článku (SSC) jako velmi významnou. Nespornou výhodou SSC složeného z grafenu a křemíkového polovodiče je oproti ostatním typům solárních článků, které jsou ve vývoji (organické či perovskitovy solární články), jednoduchý výrobní proces. Tato jednoduchost a kompatibilita se zavedenými polovodičovými technologiemi se odráží v konečném důsledku v nízké výrobní ceně. Hlavním problémem, kterým jsou Schottkyho solární články s rozhraním grafen/křemík zatíženy, je snížení účinností kolekce fotonáboje vlivem rekombinace na rozhraní. K snížení ovlivnění účinnosti rekombinací bylo rozhraní grafen/křemík upraveno 2 nm Al2O3.

In the field of applied research the combination of graphene and a semiconductor to form a Schottky solar cell (SSC) was found to be very significant. When compared to other types of solar cells being developed (organic or perovskite solar cells), the simple production process is an undisputable advantage of an SSC composed of graphene and silicon semiconductor. This simplicity and compatibility with well-established semiconductor technologies ultimately result in a low production price. The main problem relating to the Schottky solar cells with a graphene/silicon interface is the decreased efficiency of photocharge collection due to a recombination on the interface. In order to decrease the effect on the efficiency due to the recombination, the graphene/silicon interface has been modified with 2 nm Al2O3.

Grafen, Al2O3, solární článek, RTA, EBIC a EQE.

Graphene, Al2O3, solar cell, RTA, EBIC a EQE