Třecí vlastnosti nízkoteplotně plaznou cementované mikro vzorkované slitiny AISI F-1537CoCrMo
DONG, J. SVOBODA, P. KRUPKA, I. DONG, H.
Český název
Třecí vlastnosti nízkoteplotně plaznou cementované mikro vzorkované slitiny AISI F-1537CoCrMo
Anglický název
Friction property of low temperature plasma carburised micro-patterning of AISI F-1537CoCrMo alloy
Typ
abstrakt
Jazyk
en
Originální abstrakt
Corrosion-wear and iron-release are common problems that influence the biocompatibility of the materials of hip joint prosthesis. The solution to this main challenge remains is to control the following two aspects—the amount of materials shed from wearing counterparts, and the friction and lubrication between moving components, i.e. femoral head and cup. In this study, a plasma case hardened micro-geometrical patterning was created on CoCrMo surfaces with possibility of usage for long-term MoP prosthesis bearing surfaces. This surface engineered surface showed improved performance of friction property compared to untreated surface, especially in the start-and–stop mixed lubricated regime. The wear rate of the fragile patterning was increased by three to five orders of magnitude by the sequential treatment of case hardening.
Český abstrakt
Korozivní opotřebení a uvolnění kovu jsou společné problémy, které ovlivňují zdravotní nezávadnost materiálů kloubu kyčelní protézy. V této studii je popsána vytvrzená mikro-geometrická textura s možností dlouhodobého využití pro protézy.
Anglický abstrakt
Corrosion-wear and iron-release are common problems that influence the biocompatibility of the materials of hip joint prosthesis. The solution to this main challenge remains is to control the following two aspects—the amount of materials shed from wearing counterparts, and the friction and lubrication between moving components, i.e. femoral head and cup. In this study, a plasma case hardened micro-geometrical patterning was created on CoCrMo surfaces with possibility of usage for long-term MoP prosthesis bearing surfaces. This surface engineered surface showed improved performance of friction property compared to untreated surface, especially in the start-and–stop mixed lubricated regime. The wear rate of the fragile patterning was increased by three to five orders of magnitude by the sequential treatment of case hardening.
Klíčová slova česky
tření; start – stop; kyčelní kloub; smíšený režim mazání
Klíčová slova anglicky
friction; start-and–stop; hip joint; mixed lubricated regime