Mechanické vlastnosti a mikrostruktura slitiny Al-Cu zpracované pomocí SLM

Mechanical properties and microstructure of Al-Cu alloy processed by SLM

multimédia

en

Paper deal with comparison of mechanical properties and microstructure of aluminium alloy EN AW 2618A prepared using Selective Laser Melting (SLM) process and of material of the same grade processed by extrusion. It was found that defects present in microstructure of SLM material significantly affect its mechanical properties. when 0.2% proof stress was 191 MPa, UTS was 208 MPa and elongation at the break was 0.6 %, whereas measured values for extruded state were substantially higher: 0,2% proof stress was 273 MPa, UTS = 392 MPa, elongation at the break = 13.7 %.

Příspěvek se zabývá srovnáním mechaických vlastností a mikrostruktury Al slitiny EN AW 2618A vyrobené metodou SLM a stejné slitiny zpracované extrudováním.

Paper deal with comparison of mechanical properties and microstructure of aluminium alloy EN AW 2618A prepared using Selective Laser Melting (SLM) process and of material of the same grade processed by extrusion. It was found that defects present in microstructure of SLM material significantly affect its mechanical properties. when 0.2% proof stress was 191 MPa, UTS was 208 MPa and elongation at the break was 0.6 %, whereas measured values for extruded state were substantially higher: 0,2% proof stress was 273 MPa, UTS = 392 MPa, elongation at the break = 13.7 %.

Selective laser melting; aluminium alloy; extrusion; mechanical properties; microstructure; defects

19.11.2015

Žilinská universita, Slovenská Republika

Žilina, Slovenská republika

Konštrukčné materiály 2015

-–-

5