This paper deals with differences of mechanical characteristics and fracture surface morphology of magnesium alloy AZ91 in extruded state and after subsequent equal channel angular pressing (ECAP). According to results, the tensile properties are not determined by grain size only as values of the tensile strength and 0.2 proof stress were similar for both alloys despite having average grain size 15.9 μm for the extruded alloy and 1.2 μm for the ECAPed alloy. In contrast, microhardness seems to be dependant solely on the grain size. Fractographic analysis has shown changes in the damage mode from quasi-cleavage fracture in extruded state to rather ductile fracture with dimple morphology in exECAP state during tensile loading.

Tento článek se zabývá rozdíly v mechanických vlastnostech a morfologii povrchu lomu hořčíkové slitiny AZ91 v extrudovaném stavu a po následném zpracování pomocí metody ECAP (equal channel angular pressing). Podle výsledků je hodnota smluvní meze kluzu σ0,2 i pevnosti v tahu u obou slitin přibližně stejná, přestože průměrná velikost zrna extrudované slitiny je 15,9 μm, zatímco u slitiny po ECAP je pouze 1,2 μm, tahové vlastnosti tudíž nejsou dány pouze velikostí zrna (narozdíl od mikrotvrdosti). Fraktografická analýza ukázala změny v mechanismu poškození v průběhu tahového zatěžování z kvazi-štěpného lomu v případě extrudované slitiny na spíše tvárný lom po zpracovaní pomocí ECAP.

This paper deals with differences of mechanical characteristics and fracture surface morphology of magnesium alloy AZ91 in extruded state and after subsequent equal channel angular pressing (ECAP). According to results, the tensile properties are not determined by grain size only as values of the tensile strength and 0.2 proof stress were similar for both alloys despite having average grain size 15.9 μm for the extruded alloy and 1.2 μm for the ECAPed alloy. In contrast, microhardness seems to be dependant solely on the grain size. Fractographic analysis has shown changes in the damage mode from quasi-cleavage fracture in extruded state to rather ductile fracture with dimple morphology in exECAP state during tensile loading.

AZ91; microstructure; ECAP; mechanical properties; fracture behaviour