Použití metody akustické emise pro identifikaci tvorby únavových mikrotrhlin
MAZAL, P. VLAŠIC, F. KOULA, V.
Český název
Použití metody akustické emise pro identifikaci tvorby únavových mikrotrhlin
Anglický název
Use of acoustic emission method for identification of fatigue micro-cracks creation
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
This paper is a contribution to the discussion on the possibilities of identification of the time behaviour of various stages of fatigue lifetime directly during experiments using non-destructive testing methods (mainly acoustic emission method). We focus especially on detection and characterization of the transition from the stage of cycling damage accumulation to micro-cracks creation. In the past years, the laboratory of fatigue properties of FME received and published plenty of information about propagation of damage mainly in Al and Ti alloys. In this paper are presented and compared the results of new experiments with steel used for nuclear reactors and Inconel alloy. This work is focused on comparison of selected parameters of acoustic emission signal in pre-initiation and initiation stage of fatigue crack creation. Acoustic emission hits with higher stress were detected in the pre-initiation stage whereas the initiation stage hits exhibited low stress.
Český abstrakt
Tento dokument je příspěvkem k diskusi o možnostech identifikace časového chování v různých stádiích únavového života přímo v průběhu zkoušení s použitím nedestruktivních metod testování (hlavně metody akustické emise). Zaměřujeme se zejména na detekci a charakterizaci přechodu z fáze akumulace cyklického poškození k tvorbě mikrotrhlin. V posledních letech, laboratoř únavových vlastností FSI publikovala řadu informací o kumulaci poškození převážně v Al a Ti slitinách. V tomto dokumentu jsou prezentovány a porovnány výsledky nových experimentů s ocelí používanou pro jaderné reaktory a slitinou niklu. Tato práce je zaměřena na srovnání vybraných parametrů signálu akustické emise v pre-iniciační a iniciační fázi tvorby únavových trhlin.
Anglický abstrakt
This paper is a contribution to the discussion on the possibilities of identification of the time behaviour of various stages of fatigue lifetime directly during experiments using non-destructive testing methods (mainly acoustic emission method). We focus especially on detection and characterization of the transition from the stage of cycling damage accumulation to micro-cracks creation. In the past years, the laboratory of fatigue properties of FME received and published plenty of information about propagation of damage mainly in Al and Ti alloys. In this paper are presented and compared the results of new experiments with steel used for nuclear reactors and Inconel alloy. This work is focused on comparison of selected parameters of acoustic emission signal in pre-initiation and initiation stage of fatigue crack creation. Acoustic emission hits with higher stress were detected in the pre-initiation stage whereas the initiation stage hits exhibited low stress.
Klíčová slova česky
vysokocyklová únava, trhlina, akustická emise, zpracování signálů, oceli pro jaderný reaktor, Inconel
Klíčová slova anglicky
high cycle fatigue, crack, acoustic emission, signal processing, steel for nuclear reactor, Inconel
Rok RIV
2015
Vydáno
15.12.2015
Nakladatel
Elsevier
Místo
Senlis
ISSN
1877-7058
Ročník
133
Číslo
1
Strany od–do
379–388
Počet stran
10
BIBTEX
@article{BUT119766,
author="Pavel {Mazal} and František {Vlašic} and Václav {Koula},
title="Use of acoustic emission method for identification of fatigue micro-cracks creation",
year="2015",
volume="133",
number="1",
month="December",
pages="379--388",
publisher="Elsevier",
address="Senlis",
issn="1877-7058"
}