Changes in the surface layer of rolled bearing steel
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
This paper describes changes observed in bearing steel due to roller burnishing. Hydrostatic roller burnishing was selected as the most suitable method for performing roller burnishing on hardened bearing steel. The hydrostatic roller burnishing operation was applied as an additional operation after standard finishing operations. All tests were performed on samples of 100Cr6 material (EN 10132-4), and changes in the surface layer of the workpiece were then evaluated. Several simulations using finite element methods were used to obtain the best possible default parameters for the tests. The residual stress and the plastic deformation during roller burnishing were major parameters that were tested.
Český abstrakt
Tento článek popisuje změny pozorované v ložiskové oceli po aplikaci válečkování. Jako nejvhodnější metoda bylo vybráno Hydrostatické válečkování aplikované na kalené ložiskové oceli. Operace válečkování byla použita jako další operace po standardní dokončovací operaci. Všechny testy byly provedeny na vzorcích 100Cr6 materiálu (EN 10132-4), následně byly v povrchové vrstvě obrobku vyhodnoceny změny vlastností. Několik simulaci využívající metod konečných prvků bylo použito k získání co nejlepší výchozích parametrů pro testy. Zbytkové napětí a plastická deformace po válečkování byly hlavními parametry, které byly testovány.
Anglický abstrakt
This paper describes changes observed in bearing steel due to roller burnishing. Hydrostatic roller burnishing was selected as the most suitable method for performing roller burnishing on hardened bearing steel. The hydrostatic roller burnishing operation was applied as an additional operation after standard finishing operations. All tests were performed on samples of 100Cr6 material (EN 10132-4), and changes in the surface layer of the workpiece were then evaluated. Several simulations using finite element methods were used to obtain the best possible default parameters for the tests. The residual stress and the plastic deformation during roller burnishing were major parameters that were tested.
Klíčová slova anglicky
bearing steel; roller burnishing; finite element method; residual austenite; residual stress
Rok RIV
2015
Vydáno
31.10.2015
Nakladatel
ČVUT
Místo
Praha
ISSN
1210-2709
Ročník
55
Číslo
5
Strany od–do
347–351
Počet stran
5
BIBTEX
@article{BUT117928,
author="Oskar {Zemčík} and Josef {Sedlák} and Josef {Chladil},
title="Changes in the surface layer of rolled bearing steel",
year="2015",
volume="55",
number="5",
month="October",
pages="347--351",
publisher="ČVUT",
address="Praha",
issn="1210-2709"
}