The influence of surface modification on friction and lubrication mechanism under a bovine serum lubricated condition
Typ
článek v časopise ve Web of Science, Jimp
Jazyk
en
Originální abstrakt
Diamond like carbon (DLC) and micro dimple are two potential surface modification techniques that are extensively studied to be utilized into biotribological interfaces in order to reduce friction coefficient and wear rate. However, in situ observation of bovine serum lubricated DLC and micro dimpled surface contact are not well understood yet. In this study, a DLC coated and a micro dimpled steel ball rubbed against the Cr coated glass disk, where 25% bovine serum was used as a lubricant, and the temperature was maintained at 37° C. The behaviors of interface were captured using an optical interferometry and the friction coefficients were measured using a torque sensor simultaneously. The experimental results reveal that DLC/glass sliding is scuffling-free, having lowered friction coefficient, however the lubrication film formation is insignificant. On the other hand, the dimples retained lubrication and as a result, the wear of the glass disk were minimized, however friction coefficient were not reduced. Therefore, the DLC and micro dimpled individually have few improved tribological features, but their combination should be considered for maximizing the performances.
Český abstrakt
Článek se zabývá studiem tření a mazání kontaktů, jejichž třecí povrchy jsou modifikovány vrstvou DLC v kombinaci s příslušnou texturou. Je sledován vývoj součinitele tření a tloušťky mazacího filmu. Jako mazivo je použito hovězí sérum, které simuluje kloubní tekutinu.
Anglický abstrakt
Diamond like carbon (DLC) and micro dimple are two potential surface modification techniques that are extensively studied to be utilized into biotribological interfaces in order to reduce friction coefficient and wear rate. However, in situ observation of bovine serum lubricated DLC and micro dimpled surface contact are not well understood yet. In this study, a DLC coated and a micro dimpled steel ball rubbed against the Cr coated glass disk, where 25% bovine serum was used as a lubricant, and the temperature was maintained at 37° C. The behaviors of interface were captured using an optical interferometry and the friction coefficients were measured using a torque sensor simultaneously. The experimental results reveal that DLC/glass sliding is scuffling-free, having lowered friction coefficient, however the lubrication film formation is insignificant. On the other hand, the dimples retained lubrication and as a result, the wear of the glass disk were minimized, however friction coefficient were not reduced. Therefore, the DLC and micro dimpled individually have few improved tribological features, but their combination should be considered for maximizing the performances.
Klíčová slova anglicky
Diamond like carbon; micro dimple; bovine serum; friction coefficient; film formation
Vydáno
08.04.2016
Nakladatel
Taylor & Francis
Místo
United Kingdom
ISSN
1040-2004
Ročník
59
Číslo
2
Strany od–do
316–322
Počet stran
7
BIBTEX
@article{BUT116116,
author="Dipankar {Choudhury} and Fadi {Ali} and Martin {Vrbka} and Martin {Hartl} and Ivan {Křupka},
title="The influence of surface modification on friction and lubrication mechanism under a bovine serum lubricated condition",
year="2016",
volume="59",
number="2",
month="April",
pages="316--322",
publisher="Taylor & Francis",
address="United Kingdom",
issn="1040-2004"
}