Popis mechanismu zpevňování vrstevnatých keramických kompozitů
ŠTEGNEROVÁ, K. NÁHLÍK, L. HUTAŘ, P.
Český název
Popis mechanismu zpevňování vrstevnatých keramických kompozitů
Anglický název
Description of strengthening mechanism in layered ceramic composites
Typ
článek v časopise ve Scopus, Jsc
Jazyk
en
Originální abstrakt
The aim of this paper is to describe specific crack behaviour in the layered alumina-zirconia ceramic composite with strong interfaces and its strengthening mechanism. Different coefficients of thermal expansion of individual constituents of ceramic composite cause high residual stresses inside the layers during the sintering process. Compressive residual stresses can significantly influence the crack propagation through the laminate hereby improve the resistance of the material to the crack propagation. Estimation of crack behaviour in laminate was performed assuming the validity of linear elastic fracture mechanics using the criterion based on the strain energy density factor derived by Sih. This paper describes the strengthening mechanism in layered ceramic composites and prediction of their failure which contributes to better understanding of the fracture behaviour of the layered ceramic composites.
Český abstrakt
Cílem toho příspěvku je popsat specifické chování trhliny ve vrstevnatých keramických kompozitních materiálech (laminátech) na bázi Al2O3-ZrO2 se silným materiálovým rozhraním. Vlivem rozdílných koeficientů teplotní roztažnosti použitých materiálů vznikají při výrobním procesu slinování keramického kompozitu v jednotlivých vrstvách silná zbytková napětí. Tlaková zbytková napětí mohou velmi výrazně ovlivňovat šíření trhliny tělesem a výrazně napomoci ke zlepšení odolnosti proto šířenít trhlin v kompozitu. Chování trhliny v laminátu bylo popsáno za předpokladu platnosti lineárně elastické lomové mechaniky pomocí kritéria odvozeného Sihem na základě faktoru hustoty deformační energie. Tento příspěvek popisuje proces zvyšování odolnosti keramického laminátu proti šíření trhlin a predikuje jejich poškození, což přispívá k lepšímu pochopení lomového chování těchto materiálů.
Anglický abstrakt
The aim of this paper is to describe specific crack behaviour in the layered alumina-zirconia ceramic composite with strong interfaces and its strengthening mechanism. Different coefficients of thermal expansion of individual constituents of ceramic composite cause high residual stresses inside the layers during the sintering process. Compressive residual stresses can significantly influence the crack propagation through the laminate hereby improve the resistance of the material to the crack propagation. Estimation of crack behaviour in laminate was performed assuming the validity of linear elastic fracture mechanics using the criterion based on the strain energy density factor derived by Sih. This paper describes the strengthening mechanism in layered ceramic composites and prediction of their failure which contributes to better understanding of the fracture behaviour of the layered ceramic composites.
Klíčová slova česky
Vrstevnaté keramické kompozity, zbytková napětí, šíření trhliny, faktor hustoty deformační energie
Klíčová slova anglicky
Layered ceramic composites, residual stresses, crack propagation, strain energy density factor.
Rok RIV
2015
Vydáno
21.07.2015
Nakladatel
Trans Tech Publications, Switzerland
ISSN
1013-9826
Ročník
XIV
Číslo
665
Strany od–do
93–96
Počet stran
4
BIBTEX
@article{BUT115362,
author="Kateřina {Štegnerová} and Luboš {Náhlík} and Pavel {Hutař},
title="Description of strengthening mechanism in layered ceramic composites",
year="2015",
volume="XIV",
number="665",
month="July",
pages="93--96",
publisher="Trans Tech Publications, Switzerland",
issn="1013-9826"
}