Biodegradabilní vlastnosti slitiny AZ31 s povlakem na bázi DICALCIUM PHOSPHATE DIHYDRATE
Filip Pastorek, Miroslav Omasta, Lenka Bukovinová, Pavel Doležal, Branislav Hadzima
Český název
Biodegradabilní vlastnosti slitiny AZ31 s povlakem na bázi DICALCIUM PHOSPHATE DIHYDRATE
Anglický název
BIODEGRADATION PROPERTIES OF AZ31 MAGNESIUM ALLOY COATED BY DICALCIUM PHOSPHATE DIHYDRATE
Typ
článek v časopise ve Scopus, Jsc
Jazyk
en
Originální abstrakt
Biodegradation properties of magnesium and its alloys that can be used for implants are not satisfactory and cause serious problems. These problems can be solved by biodegradable surface coatings. Evaluation of biodegradation process of Mg-3Al-1Zn alloy surfaces after grinding and grinding followed by potential controlled electrodeposition of dicalcium phosphate dihydrate (DCPD) was investigated by electro-chemical impedance spectroscopy measurements in this study. The potentiostatic electrodeposition treatment process was performed in water solutionof Ca(NO3)2.4H2, NH4H2PO4and H2O2. The corrosion process on treated and nontreated samples after various exposure times wasevaluated in 0.9% NaCl solution simulating body fluid environment at 37 °C.
Český abstrakt
Biodegradačních vlastnosti hořčíku a jeho slitin, které mohou být použity pro implantáty nejsou uspokojivé, a způsobit vážné problémy. Tyto problémy mohou být vyřešeny pomocí biologicky rozložitelných povrchových povlaků. Hodnocení biodegradační proces povrchů Mg-3Al-1Zn slitin po broušení a broušení následuje potenciální řízeným elektroforetické hydrogenfosforečnan vápenatý dihydrát (DCPD) byl vyšetřován elektrochemických měření impedanční spektroskopie v této studii. Potenciostatické proces galvanické ošetření se provádí ve vodě solutionof Ca (NO 3) 2.4H2, NH4H2PO4and H2O2. Proces koroze na ošetřených a neošetřených vzorků po různé expoziční časy wasevaluated v 0,9% roztoku chloridu sodného simulující tělesné tekutině prostředí, při teplotě 37 ° C.
Anglický abstrakt
Biodegradation properties of magnesium and its alloys that can be used for implants are not satisfactory and cause serious problems. These problems can be solved by biodegradable surface coatings. Evaluation of biodegradation process of Mg-3Al-1Zn alloy surfaces after grinding and grinding followed by potential controlled electrodeposition of dicalcium phosphate dihydrate (DCPD) was investigated by electro-chemical impedance spectroscopy measurements in this study. The potentiostatic electrodeposition treatment process was performed in water solutionof Ca(NO3)2.4H2, NH4H2PO4and H2O2. The corrosion process on treated and nontreated samples after various exposure times wasevaluated in 0.9% NaCl solution simulating body fluid environment at 37 °C.
Klíčová slova anglicky
Magnesium alloy, electrodeposition, calcium phosphate, electrochemical impedance spectroscopy.
Rok RIV
2014
Vydáno
03.03.2014
Nakladatel
University of Zilina
Místo
Žilina, Slovenská republika
ISSN
1335-4205
Ročník
16
Číslo
3A
Strany od–do
189–193
Počet stran
5
BIBTEX
@article{BUT113440,
author="Pavel {Doležal},
title="BIODEGRADATION PROPERTIES OF AZ31 MAGNESIUM ALLOY COATED BY DICALCIUM PHOSPHATE DIHYDRATE",
year="2014",
volume="16",
number="3A",
month="March",
pages="189--193",
publisher="University of Zilina",
address="Žilina, Slovenská republika",
issn="1335-4205"
}